共沈法によるバナジウムドープBi_4Ti_3O_(12)粉末の合成および焼結セラミックの誘電特性

Preparation of Vanadium Doped Bi_4Ti_3O_(12) Powder by Co-precipitation and Dielectric Property of Sintered Ceramics

著者 (5件)： TANG QingYuan (State Key Lab of High Performance Ceramics and Superfine Microstructure, Shanghai Inst. of Ceramics, Chinese Acad. ...) ,  LI YaoGang (Coll. of Material Sci. and Engineering, DongHua Univ., Shanghai) ,  KAN YanMei (State Key Lab of High Performance Ceramics and Superfine Microstructure, Shanghai Inst. of Ceramics, Chinese Acad. ...) ,  ZHANG GuoJun (State Key Lab of High Performance Ceramics and Superfine Microstructure, Shanghai Inst. of Ceramics, Chinese Acad. ...) ,  WANG PeiLing (State Key Lab of High Performance Ceramics and Superfine Microstructure, Shanghai Inst. of Ceramics, Chinese Acad. ...)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 22  号： 4  ページ： 595-598  発行年： 2007年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： バナジウムドープBi_4Ti_3O_(12)粉末を共沈法により合成し,その相発達過程,微細構造および焼結挙動を調べた。その結果,粒径が100nm未満のBi_4Ti_3O_(12)結晶相が,前駆体の550°Cでのか焼により得られ,これは,従来の固相反応よりも250°C低いことが分かった。この粉末は,優れた焼結活性を有し,焼結試料のかさ密度は,900°Cで1h焼結した場合理論値の96%に達した。固相反応合成の材料と比べて,共沈粉末から作製した試料は,また低い誘電損失を有していた。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *チタン酸塩 ,  *ビスマス化合物 ,  *バナジウム化合物 ,  *ドーピング ,  *共沈 ,  化学合成 ,  相 ,  焼結性 ,  容積重 ,  *誘電損失 ,  *セラミック ,  焼結体
準シソーラス用語： かさ密度

分類 (3件)： 塩基,金属酸化物  (CD01030Z) ,  セラミック・磁器の性質  (YC03030G) ,  誘電体一般  (BM05010F)

タイトルに関連する用語 (6件)： 共沈法 ,  バナジウム ,  ドープ ,  粉末 ,  焼結セラミック ,  誘電特性