熱感応性の毛髪状混成粒子内のAgナノ粒子の生成

Formation of Ag nanoparticles within the thermosensitive hairy hybrid particles

著者 (6件)： LEI Zhongli (Key Lab. of Applied Surface and Colloid Chemistry (Shaanxi Normal University), Ministry of Education, School of ...) ,  LI Na (Key Lab. of Applied Surface and Colloid Chemistry (Shaanxi Normal University), Ministry of Education, School of ...) ,  LIN Lin (Key Lab. of Applied Surface and Colloid Chemistry (Shaanxi Normal University), Ministry of Education, School of ...) ,  JIA Yongming (Key Lab. of Applied Surface and Colloid Chemistry (Shaanxi Normal University), Ministry of Education, School of ...) ,  PANG Xiaolong (Key Lab. of Applied Surface and Colloid Chemistry (Shaanxi Normal University), Ministry of Education, School of ...) ,  REN Na (Key Lab. of Applied Surface and Colloid Chemistry (Shaanxi Normal University), Ministry of Education, School of ...)
資料名： Materials Letters  (Materials Letters)
巻： 63  号： 12  ページ： 975-977  発行年： 2009年05月15日 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ここでは,複合コア・シェル粒子の作製を報告する。この作製は,実際には,金属-ブロック共重合体ナノ複合材の生成のためのテンプレートとしての,ポリ(N-イソプロピルアクリルアミド)基の両親媒性ブロック共重合体の自己集合である。両親媒性で熱感応性のポリマーのコロイド粒子の中に埋め込んだAgナノ粒子を用いて,有機-無機複合材料を作製した。非凝集のAgナノ粒子の導入を促進するために,ポリ(N-イソプロピルアクリルアミド)(NIPAM)ブロックとポリスチレンとの温度応答性小球体を合成した。ポリエチレンイミン(PEI)が,Agイオン(Agナノ粒子)とポリ(スチレン-b-N-イソプロピルアクリルアミド)(PS-b-PNIPAM)コロイドの間のリンカとして,また,Agナノ粒子の生成の還元剤として機能した。透過電子顕微鏡(TEM)測定によってナノ構造を確認した。¹HNMRとFTIRで,得られたナノ試料をキャラクタライズした。これらの刺激感受性混成ミクロ球体は,生体組織工学や薬剤配送のような生物医学領域に潜在的用途を持つと思われる。Copyright 2009 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ナノ複合材料 ,  高分子有機-無機ハイブリッド ,  *ポリアクリルアミド ,  ナノ粒子 ,  *銀 ,  自己集合 ,  共重合体 ,  ポリスチレン ,  温度依存性
準シソーラス用語： ポリ(N-イソプロピルアクリルアミド)

分類 (2件)： 高分子固体の構造と形態学  (CG02022M) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (2件)： 熱感応 ,  Agナノ粒子