背圧等チャンネル角押出による超微細Al粒子圧密中にその場生成したナノ構造Al-Al₂O₃複合材料

Nanostructured Al-Al₂O₃ composite formed in situ during consolidation of ultrafine Al particles by back pressure equal channel angular pressing

著者 (5件)： XU W. (Dep. of Mechanical Engineering and ARC Centre of Excellence for Design in Light Metals, Univ. of Melbourne, Vic. ...) ,  WU X. (Dep. of Mechanical Engineering and ARC Centre of Excellence for Design in Light Metals, Univ. of Melbourne, Vic. ...) ,  HONMA T. (Australian Key Centre for Microscopy and Microanalysis, Univ. of Sydney, NSW 2006, AUS) ,  RINGER S.p. (Australian Key Centre for Microscopy and Microanalysis and ARC Centre of Excellence for Design in Light Metals ...) ,  XIA K. (Dep. of Mechanical Engineering and ARC Centre of Excellence for Design in Light Metals, Univ. of Melbourne, Vic. ...)
資料名： Acta Materialia  (Acta Materialia)
巻： 57  号： 14  ページ： 4321-4330  発行年： 2009年08月 
JST資料番号： A0316A  ISSN： 1359-6454  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 背圧等チャンネル角押出(BP-ECAP)法を用いて超微細純Al粒子を完全稠密バルク材料に圧密した。圧密は200MPaの背圧にて400°Cで実施した。成形直後の粒子から4パスで,大部分がAl及びγ-Al₂O₃ナノ結晶,少量の超微細Al結晶及び非晶質アルミナから成る完全稠密Al-Al₂O₃複合材料を製造した。これに対し,18及び24か月の間保持した時効粒子からの圧密は達成できなかった。ナノ構造の生成はECAP中の強度のせん断変形及びその場酸化間の相互作用に起因するものであった。ナノ構造材の抗張力は圧縮において約740MPaに達し,破壊までの塑性歪は約1%の水準であった。超微細粒子は,互いの間の滑りではなく,形状が変わるほどせん断を受ける場合ECAPにより十分圧密可能であることを実証した。Copyright 2009 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： 圧密 ,  *押出 ,  背圧 ,  超微粒子 ,  *アルミニウム ,  焼結 ,  *ナノ複合材料 ,  *γアルミナ ,  非晶質 ,  酸化 ,  引張強さ ,  塑性歪 ,  剪断 ,  圧粉 ,  焼結体 ,  加工 ,  塑性変形 ,  ナノ結晶 ,  SPD【塑性】
準シソーラス用語： ECAP法 ,  強歪加工 ,  重塑性変形

分類 (2件)： 分散冶金  (WC02040I) ,  分散強化合金  (WE04030R)

タイトルに関連する用語 (8件)： 背圧 ,  等チャンネル角押出 ,  超微細 ,  Al ,  圧密 ,  ナノ構造 ,  Al2O3 ,  複合材料