高電力Liイオン電池サイクル試験後の正極の研究 I XANESを用いる電力低下機構の研究方法

Investigation of positive electrodes after cycle testing of high-power Li-ion battery cells I. An approach to the power fading mechanism using XANES

著者 (5件)： KOBAYASHI Hironori (Res. Inst. for Ubiquitous Energy Devices, National Inst. of Advanced Industrial Sci. and Technol. (AIST), Ikeda ...) ,  SHIKANO Masahiro (Res. Inst. for Ubiquitous Energy Devices, National Inst. of Advanced Industrial Sci. and Technol. (AIST), Ikeda ...) ,  KOIKE Shinji (Res. Inst. for Ubiquitous Energy Devices, National Inst. of Advanced Industrial Sci. and Technol. (AIST), Ikeda ...) ,  SAKAEBE Hikari (Res. Inst. for Ubiquitous Energy Devices, National Inst. of Advanced Industrial Sci. and Technol. (AIST), Ikeda ...) ,  TATSUMI Kuniaki (Res. Inst. for Ubiquitous Energy Devices, National Inst. of Advanced Industrial Sci. and Technol. (AIST), Ikeda ...)
資料名： Journal of Power Sources  (Journal of Power Sources)
巻： 174  号： 2  ページ： 380-386  発行年： 2007年12月06日 
JST資料番号： B0703B  ISSN： 0378-7753  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 酸化コバルトニッケル(LiNi_0.73Co_0.17Al_0.10O₂)正極と非黒鉛化炭素(ハードカーボン)負極を備える円筒リチウムイオン(Liイオン)電池をサイクル試験により劣化させた。劣化電池を分解調査した;電池の電力低下の原因を明らかにするため,正極に多くの注意を払った。X線近吸収端構造(XANES)分析は,電極の結晶構造がその表面で菱面体晶から立方晶対称に変化したことを実証した。さらに,サイクル試験後に炭酸リチウム(Li₂CO₃)の膜が正極表面を覆った。X線光電子分光法(XPS)と赤外分光法(IR),グロー放電発光分光法(GD-OES)測定を組み合わせ用いて,サイクル試験中に正極の表面構造内で起きる変化の基本モデルを構築した。電気化学的に不活性な立方晶相と炭酸リチウム膜が共に正極表面で現れることは,正極の電力低下を強める重大な要因である。Copyright 2007 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *リチウムイオン電池 ,  *電極材料 ,  *劣化 ,  *XANES ,  リチウム化合物 ,  ニッケル化合物 ,  コバルト化合物 ,  酸化物 ,  アルミニウム化合物 ,  炭素電極 ,  充放電サイクル ,  層状化合物 ,  結晶構造