ポリアクリロニトリルで強化した繊維ポリスチレンマットの機械的挙動および濡れ挙動

Mechanical and wettable behavior of polyacrylonitrile reinforced fibrous polystyrene mats

著者 (8件)： SUN Min (Engineering Res. Center of Technical Textiles, Ministry of Education, Donghua Univ., Shanghai 201620, CHN) ,  SUN Min (Nanomaterials Res. Center, Modern Textile Inst., Donghua Univ., Shanghai 200051, CHN) ,  SUN Min (Coll. of Textiles, Donghua Univ., Shanghai 201620, CHN) ,  LI Xiaohong (Coll. of Textiles, Donghua Univ., Shanghai 201620, CHN) ,  DING Bin (Engineering Res. Center of Technical Textiles, Ministry of Education, Donghua Univ., Shanghai 201620, CHN) ,  DING Bin (Nanomaterials Res. Center, Modern Textile Inst., Donghua Univ., Shanghai 200051, CHN) ,  YU Jianyong (Nanomaterials Res. Center, Modern Textile Inst., Donghua Univ., Shanghai 200051, CHN) ,  SUN Gang (Fibers and Polymer Sci., Univ. of California, Davis, CA 95616, USA)
資料名： Journal of Colloid and Interface Science  (Journal of Colloid and Interface Science)
巻： 347  号： 1  ページ： 147-152  発行年： 2010年07月01日 
JST資料番号： C0279A  ISSN： 0021-9797  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,複数シリンジエレクトロスピニング技法によってポリアクリロニトリル(PAN)強化超疎水性繊維ポリスチレン(PS)マットを作製した。PS/PANのシリンジ数比を調整することによってブレンドマット中のPS/PANの組成比を制御することができた。PS/PANのシリンジ数比を4/0から1/3に減らすと得られた繊維マットの水接触角(WCA)が155°から143°に減少した。繊維PSマット中にPANナノファイバーの成分を加えるとPSマットの機械的特性が大幅に向上した。3/1(PS/PAN)の臨界シリンジ比でマット表面は150°のWCAを示し,引張強さは純PSマットと比べて3倍に増加した。さらに,電界放出型走査電子顕微鏡法(FE-SEM),Fourier変換赤外(FT-IR)および機械的特性の結果は複数シリンジエレクトロスピニング技法が大規模の良好に分散したブレンド繊維マットを作製する有効な手法であることを示した。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ポリアクリロニトリル ,  *ポリスチレン ,  *マット ,  濡れ ,  *繊維 ,  疎水性 ,  エレクトロスピニング ,  ナノファイバ
準シソーラス用語： *強化繊維 ,  超疎水性

分類 (2件)： 高分子固体の力学的性質  (CG02023D) ,  ポリスチレン  (YH07120V)

タイトルに関連する用語 (8件)： ポリアクリロニトリル ,  強化 ,  繊維 ,  ポリスチレン ,  マット ,  機械的挙動 ,  濡れ ,  挙動