Armstrong ProcessCP-Ti及びTi-6Al-4V粉末を用いた低コストチタンニヤネットシェイプ製造

Low Cost Titanium Near-Net-Shape Manufacturing Using Armstrong Process CP-Ti and Ti-6Al-4V Powders

著者 (14件)： YAMAMOTO Yukinori (Oak Ridge National Lab., TN, USA) ,  PETER William H. (Oak Ridge National Lab., TN, USA) ,  SABAU Adrian S. (Oak Ridge National Lab., TN, USA) ,  GORTI Sarma B. (Oak Ridge National Lab., TN, USA) ,  KIGGANS Jim O. (Oak Ridge National Lab., TN, USA) ,  NUNN Stephen D. (Oak Ridge National Lab., TN, USA) ,  CLARK Michael B. (Oak Ridge National Lab., TN, USA) ,  BLUE Craig A. (Oak Ridge National Lab., TN, USA) ,  BARNES John E. (Lockheed Martin Aeronautics Co., GA) ,  HENRY Chad (Lockheed Martin Aeronautics Co., GA) ,  CAPONE Joe A. (AMETEK, Inc, CT) ,  PALIWAL Muktesh (AMETEK, Inc, CT) ,  FULLER Brian (Cristal US, Inc., IL) ,  AKHTAR Kamal (Cristal US, Inc., IL)
資料名： Advances in Powder Metallurgy & Particulate Materials  (Advances in Powder Metallurgy & Particulate Materials)
巻： 2010  号： Vol.1  ページ： 3.24-3.33  発行年： 2010年 
JST資料番号： E0252C  ISSN： 1065-5824  資料種別： 会議録 (C)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究は,Armstrong Prosessで作製したCP-Ti及びTi-6Al-4V合金粉を用いて,ニヤネットシェイプ成形試験を行った。ボールミル処理により,タップ密度が約8%から約30%に大幅に増加した。プレス-焼結処理後の密度は,ボールミル処理やプレス方法よりもプレス圧の影響を強く受けた。容器無し空気静水圧鍛造(PIF)処理及びHIP処理により,外表面に連結した開気孔は消滅し,焼結後密度は理論密度の99.6%に達した。本試験結果から,Armstrong Processで作製したチタン及びチタン合金粉は,欠陥の無いニヤネットPM製品の原料として利用できる事が明らかになった。

シソーラス用語： チタン ,  *Ti-6Al-4V合金 ,  合金粉 ,  酸化チタン ,  *near net shape法 ,  処理 ,  摩砕 ,  焼結 ,  HIP【ホットプレス】 ,  原料 ,  密度 ,  焼結鍛造 ,  CIP【粉末成形】 ,  粉末冶金 ,  圧粉 ,  圧密 ,  粉末冶金製品
準シソーラス用語： ボールミル処理