Fe/Ba(Fe_1-xCo_x)₂As₂二層膜の結晶品質と輸送特性に及ぼすFeバッファ層厚の影響

Influence of Fe buffer thickness on the crystalline quality and the transport properties of Fe/Ba(Fe_1-xCo_x)₂As₂ bilayers

著者 (11件)： IIDA K. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  HAINDL S. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  THERSLEFF T. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  HAENISCH J. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  KURTH F. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  KIDSZUN M. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  HUEHNE R. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  MOENCH I. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  SCHULTZ L. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  HOLZAPFEL B. (IFW Dresden, P. O. Box 270116, 01171 Dresden, DEU) ,  HELLER R. (Inst. of Ion Beam Physics and Materials Res., FZ Dresden-Rossendorf, Bautzner Landstr. 400, 01328 Dresden, DEU)
資料名： Applied Physics Letters  (Applied Physics Letters)
巻： 97  号： 17  ページ： 172507  発行年： 2010年10月25日 
JST資料番号： H0613A  ISSN： 0003-6951  CODEN： APPLAB  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： Feバッファ層の導入は,CoドープBaFe₂As₂(Ba-122)のエピタキシャル成長膜を得る有望な方法であった。けれども,CoドープBa-122の結晶品質と超伝導特性はFeバッファ層厚,dFeによって影響を受けた。dFe=15nmの場合Fe/Ba-122二層膜は良く配向成長し,自己場中,12KでJ_c=0.45MAcm^-2の高い値を有したが,同じ温度でdFe=4nmの場合の二層膜は,J_c=61000Acm^-2と低かった。これは,粒界の存在によるものであった。(翻訳著者抄録)

シソーラス用語： *高温超伝導体 ,  鉄 ,  *バッファ層 ,  バリウム化合物 ,  *鉄化合物 ,  コバルト化合物 ,  ヒ素化合物 ,  コバルト ,  ドーピング ,  多層膜 ,  品質 ,  レーザ蒸着 ,  酸化マグネシウム ,  基板 ,  エピタクシー ,  電気抵抗率 ,  温度 ,  磁場 ,  依存性 ,  結晶粒界 ,  配向 ,  成長 ,  臨界電流密度 ,  Rutherford後方散乱 ,  透過型電子顕微鏡 ,  パルスレーザ蒸着
準シソーラス用語： 二層膜 ,  結晶品質

分類 (1件)： 金属系超伝導体の物性  (BM04022R)

タイトルに関連する用語 (7件)： Fe ,  Ba ,  二層膜 ,  結晶品質 ,  輸送特性 ,  バッファ ,  層厚