電着Ptナノ粒子のモルホロジー的特徴と高分子電解質ギ酸燃料電池のアノード触媒としての用途

Morphological features of electrodeposited Pt nanoparticles and its application as anode catalysts in polymer electrolyte formic acid fuel cells

著者 (6件)： JEON Hongrae (Electrochemical Reaction & Technol. Lab. (ERTL), Dep. of Environmental Sci. and Engineering, GIST, Gwangju 500-712, KOR) ,  JOO Jiyong (Electrochemical Reaction & Technol. Lab. (ERTL), Dep. of Environmental Sci. and Engineering, GIST, Gwangju 500-712, KOR) ,  KWON Youngkook (Electrochemical Reaction & Technol. Lab. (ERTL), Dep. of Environmental Sci. and Engineering, GIST, Gwangju 500-712, KOR) ,  UHM Sunghyun (Ertl Center for Electrochemistry and Catalysis, GIST, Gwangju 500-712, KOR) ,  LEE Jaeyoung (Electrochemical Reaction & Technol. Lab. (ERTL), Dep. of Environmental Sci. and Engineering, GIST, Gwangju 500-712, KOR) ,  LEE Jaeyoung (Ertl Center for Electrochemistry and Catalysis, GIST, Gwangju 500-712, KOR)
資料名： Journal of Power Sources  (Journal of Power Sources)
巻： 195  号： 18  ページ： 5929-5933  発行年： 2010年09月15日 
JST資料番号： B0703B  ISSN： 0378-7753  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 炭素基板上の電着Ptナノ粒子は,加えられた電位に依存して種々のモルホロジーを示す。Ptの樹状,ピラミッド状,カリフラワー状および半球状モルホロジーが-0.2~0.3V(Ag/AgClに対して)の電位範囲において生成され,その粒径は8~26nmに分布する。加えられた電位-0.2Vにおいて,20nm以上の樹状の塊状粒子が生成され,一方,0.2Vの小さな蒸着電位は10nm以下のPtの密な半球状の構造を発生する。ギ酸の電解触媒は酸化に対する種々のPtの影響を示す。結果として炭素紙上において約14nmの平均粒子を有するPtナノ粒子の均一な分布は,容量に対する大きな面積比となり,燃料電池用途におけるより良好な電力性能となる。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *電着 ,  ナノ粒子 ,  白金 ,  *液体燃料電池 ,  高分子電解質 ,  アノード ,  触媒活性 ,  アノード酸化 ,  電極触媒 ,  電流電圧特性
準シソーラス用語： *直接ギ酸燃料電池 ,  分極曲線

分類 (1件)： 燃料電池  (YB04040V)

タイトルに関連する用語 (8件)： 電着 ,  Ptナノ粒子 ,  モルホロジー ,  高分子電解質 ,  ギ酸 ,  燃料電池 ,  アノード触媒 ,  用途