新規界面重合手法による薄膜複合逆浸透膜の合成およびキャラクタリゼーション

Synthesis and characterization of thin film composite reverse osmosis membranes via novel interfacial polymerization approach

著者 (7件)： ZOU Hao (National Lab. of Molecular Sciences, Inst. of Chemistry, Chinese Acad. of Sciences (ICCAS), Beijing 100190, CHN) ,  ZOU Hao (Vontron Technol. Co., Ltd., Beijing 102249, CHN) ,  JIN Yan (Vontron Technol. Co., Ltd., Beijing 102249, CHN) ,  YANG Jun (Zhuzhou Times New Material Technol. Co., Ltd., Zhuzhou 412007, CHN) ,  DAI Hongjun (National Lab. of Molecular Sciences, Inst. of Chemistry, Chinese Acad. of Sciences (ICCAS), Beijing 100190, CHN) ,  YU Xiaolan (National Lab. of Molecular Sciences, Inst. of Chemistry, Chinese Acad. of Sciences (ICCAS), Beijing 100190, CHN) ,  XU Jian (National Lab. of Molecular Sciences, Inst. of Chemistry, Chinese Acad. of Sciences (ICCAS), Beijing 100190, CHN)
資料名： Separation and Purification Technology  (Separation and Purification Technology)
巻： 72  号： 3  ページ： 256-262  発行年： 2010年05月11日 
JST資料番号： T0428B  ISSN： 1383-5866  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,優れた特性を持つ薄膜複合逆浸透(RO)膜を調製するため,新規界面重合手法を適用した。膜の表面は,走査型電子顕微鏡(SEM),減衰全反射赤外(ATR-IR)およびX線光電子分光(XPS)によりキャラクタリゼーションした。その結果,新規界面重合手法により調製した膜は,伝統的な界面重合手法により得られる膜よりも,より滑らかな表面を持つことを示した。新規界面重合手法により生成した膜の活性スキン層の最上表面には,伝統的な界面重合手法により合成されるカルボン酸基(-COOH)と比較し,多量のアミノ基(-NH₂)が存在した。更に,新規界面重合手法により作製した膜は,伝統的な界面重合手法により調製したものよりも,より良好な防汚性を示した。良好な膜性能特性を持つ薄膜複合RO膜を調製する,独特でかつシンプルな方法をデモンストレーションした。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *界面重合 ,  *半透膜 ,  複合膜 ,  高分子薄膜 ,  ポリアミド ,  汚損 ,  表面構造 ,  電子顕微鏡観察 ,  *逆浸透膜
準シソーラス用語： 表面モルホロジー

分類 (2件)： 膜分離  (XD02120Z) ,  単独重合  (CG04020S)

タイトルに関連する用語 (5件)： 界面重合 ,  手法 ,  薄膜 ,  複合逆浸透膜 ,  キャラクタリゼーション