WO₃-SnO₂ナノコンポジットの調製およびそのNO₂に対するセンサ特性の評価

Preparation, characterization of WO₃-SnO₂ nanocomposites and their sensing properties for NO₂

著者 (6件)： BAI Shouli (State Key Lab. of Chemical Resource Engineering, Beijing Univ. of Chemical Technol., 15 Beisanhuan East Road ...) ,  LI Dianqing (State Key Lab. of Chemical Resource Engineering, Beijing Univ. of Chemical Technol., 15 Beisanhuan East Road ...) ,  HAN Dongmei (State Key Lab. of Chemical Resource Engineering, Beijing Univ. of Chemical Technol., 15 Beisanhuan East Road ...) ,  LUO Ruixian (State Key Lab. of Chemical Resource Engineering, Beijing Univ. of Chemical Technol., 15 Beisanhuan East Road ...) ,  CHEN Aifan (State Key Lab. of Chemical Resource Engineering, Beijing Univ. of Chemical Technol., 15 Beisanhuan East Road ...) ,  CHUNG Chiun Liu (Dep. of Chemical Engineering, Case Western Reserve Univ., Cleveland, OH 44106, USA)
資料名： Sensors and Actuators. B. Chemical  (Sensors and Actuators. B. Chemical)
巻： 150  号： 2  ページ： 749-755  発行年： 2010年10月28日 
JST資料番号： T0967A  ISSN： 0925-4005  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 各種組成のWO₃-SnO₂ナノ複合体を,塩化スズと前駆体としてのメタタングステン酸アンモニウム水和物を用いて制御二段ゾル-沈殿法による調製に成功した。材料の性能を各種解析手法で評価した。ナノコンポジットに基づくセンサを使用して,100から300°Cの動作温度範囲でNO₂を検出した。このときの応答は,空気-NO₂混合物に対する空気(Rg/Ra)中でのセンサ抵抗の比として定義した。実験結果より,20mol%WO₃-SnO₂ナノベースセンサは,200°Cの動作温度で186から200ppmのNO₂に最高の応答性を示した。さらにドーパントとしてZnを3wt%,ならびにMgOを表面改質剤として3wt%ドープすることにより,それぞれ251と418に増大し,最適動作温度は150に低下した。ドーピング効果と検出機構を,昇温脱離(TPD)およびX線光電子分光法(XPS)分析により検討した。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.