Ti-5Al-5Mo-5V-3Crにおけるαの析出に及ぼす炭素の影響

The influence of carbon on precipitation of α in Ti-5Al-5Mo-5V-3Cr

著者 (4件)： WAIN N. (IRC in Materials, Coll. of Engineering and Physical Sciences, Univ. of Birmingham, Edgbaston, Birmingham, B15 2TT, GBR) ,  HAO X.j. (IRC in Materials, Coll. of Engineering and Physical Sciences, Univ. of Birmingham, Edgbaston, Birmingham, B15 2TT, GBR) ,  RAVI G.a. (IRC in Materials, Coll. of Engineering and Physical Sciences, Univ. of Birmingham, Edgbaston, Birmingham, B15 2TT, GBR) ,  WU X. (IRC in Materials, Coll. of Engineering and Physical Sciences, Univ. of Birmingham, Edgbaston, Birmingham, B15 2TT, GBR)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 527  号： 29-30  ページ： 7673-7683  発行年： 2010年11月15日 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 準安定β-Ti合金(溶体化処理後急冷したTi-5Al-5Mo-5V-3Cr)の時効応答に及ぼす炭素添加の影響を走査・透過電子顕微鏡と微小硬さ試験機で調べた。0~0.1重量%の炭素を添加した合金を作製し,溶体化温度,時効温度,時間,加熱速度を変えて,ミクロ組織の進展を究明した。その結果,炭素の少量添加は,β溶体化処理した後500~600°Cで時効させた合金に大きな影響を及ぼし,α相の析出を微細かつ均一にした。特に炭素は粗いαが結晶粒界に形成する傾向を減らし,低い時効温度で等温ω相の形成に強い影響を及ぼすことが分かった。炭素無添加合金では,徐熱又は段階的な加熱によって多量のα相を微細化できることもわかった。炭素添加による微細化の機構は遅い加熱による機構とは異なるようである。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *炭素 ,  *析出 ,  *α相 ,  *チタン合金 ,  アルミニウム含有合金 ,  モリブデン含有合金 ,  バナジウム含有合金 ,  クロム含有合金 ,  溶体化処理 ,  焼入 ,  準安定相 ,  硬度 ,  金属組織 ,  *時効処理 ,  結晶粒界 ,  *ω相 ,  時間 ,  含有量 ,  温度依存性 ,  結晶粒微細化 ,  加熱速度
準シソーラス用語： 時効温度

分類 (1件)： 組織的硬化現象  (WB01020C)

タイトルに関連する用語 (2件)： 析出 ,  炭素