ポリエーテルグラフト化エポキシド系ポリシロキサンで改質したエポキシ樹脂の衝撃抵抗性と熱特性の同時向上挙動

Simultaneously Increasing Impact Resistance and Thermal Properties of Epoxy Resins Modified by Polyether-Grafted-Epoxide Polysiloxane

著者 (9件)： LIU Weiqu (Guangzhou Inst. Chemistry, Chinese Acad. Sci., Guangzhou, CHN) ,  MA Songqi (Guangzhou Inst. Chemistry, Chinese Acad. Sci., Guangzhou, CHN) ,  WANG Zhengfang (Guangzhou Inst. Chemistry, Chinese Acad. Sci., Guangzhou, CHN) ,  HU Chaohui (Guangzhou Inst. Chemistry, Chinese Acad. Sci., Guangzhou, CHN) ,  TANG Chunyi (Guangzhou Inst. Chemistry, Chinese Acad. Sci., Guangzhou, CHN) ,  MA Songqi (Graduate Univ. Chinese Acad. Sci., Beijing, CHN) ,  WANG Zhengfang (Graduate Univ. Chinese Acad. Sci., Beijing, CHN) ,  HU Chaohui (Graduate Univ. Chinese Acad. Sci., Beijing, CHN) ,  TANG Chunyi (Graduate Univ. Chinese Acad. Sci., Beijing, CHN)
資料名： Polymer-Plastics Technology and Engineering  (Polymer-Plastics Technology and Engineering)
巻： 49  号： 4/6  ページ： 467-473  発行年： 2010年02月15日 
JST資料番号： B0866A  ISSN： 0360-2559  CODEN： PPTEC7  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： エポキシ樹脂は電子部品の充填材料に汎用し,理由は機械や電気,熱,化学特性が良好なためである。然し架橋密度が高く脆性破壊が発生し易い為,電子部品を開発する際の要求仕様に適合しない。ビスフェノールAのジグリシジルエーテルを改質する為,ポリメチルヒドロシロキサンやアリルグリシジルエーテル,アリルポリオキシエチレンポリオキシプロピレンを併用し,ポリエーテルグラフト化エポキシド系ポリシロキサンを合成した。走査電子顕微鏡や示差走査熱量測定,熱重量分析,衝撃試験で形状や熱特性,破壊挙動を実測した。グラフト化したポリシロキサンはエポキシ系マトリックス内に均一分散し,改質したエポキシ樹脂は衝撃抵抗性や熱特性が同時に向上した。

シソーラス用語： *ビスフェノールAエポキシ樹脂 ,  破壊試験 ,  グラフト共重合体 ,  *ポリエーテル ,  *ポリシロキサン ,  衝撃強さ ,  熱安定性 ,  ヒドロシリル化 ,  ポリエチレンオキシド ,  形状測定 ,  示差走査熱量測定 ,  熱重量分析 ,  走査電子顕微鏡
準シソーラス用語： エポキシド ,  ポリオキシエチレンポリオキシプロピレンブロックコポリマー ,  ポリメチルヒドロシロキサン

分類 (4件)： エポキシ樹脂  (YH07040I) ,  ゴム・プラスチック材料試験  (HB03000F) ,  ゴム・プラスチック材料  (HC04030W) ,  共重合  (CG04030D)

物質索引 (2件)： アリルグリシジルエーテル ,  ジグリシジルエーテル

タイトルに関連する用語 (7件)： エポキシド ,  ポリシロキサン ,  改質 ,  エポキシ樹脂 ,  衝撃抵抗 ,  熱特性 ,  挙動