コア-シェルナノ粒子PMMA/PTFEナノコンポジット中のPTFEの多重結晶化挙動

On the Multiple Crystallization Behavior of PTFE in PMMA/PTFE Nanocomposites from Core-Shell Nanoparticles

著者 (9件)： LAUS Michele (Universita del Piemonte Orientale “A. Avogadro”, Alessandria, ITA) ,  SPARNACCI Katia (Universita del Piemonte Orientale “A. Avogadro”, Alessandria, ITA) ,  ANTONIOLI Diego (Universita del Piemonte Orientale “A. Avogadro”, Alessandria, ITA) ,  DEREGIBUS Simone (Universita del Piemonte Orientale “A. Avogadro”, Alessandria, ITA) ,  KAPELIOUCHKO Valerj (Solvay Solexis SpA, Alessandria, ITA) ,  PALAMONE Giovanna (Solvay Solexis SpA, Alessandria, ITA) ,  POGGIO Tiziana (Solvay Solexis SpA, Alessandria, ITA) ,  ZUCCHERI Giampaolo (Universita di Bologna, Bologna, ITA) ,  PASSERI Rosita (Universita di Bologna, Bologna, ITA)
資料名： Journal of Polymer Science. Part B. Polymer Physics  (Journal of Polymer Science. Part B. Polymer Physics)
巻： 48  号： 5  ページ： 548-554  発行年： 2010年03月01日 
JST資料番号： C0346B  ISSN： 0887-6266  CODEN： JPLPAY  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： PTFE(径33nm)ラテックスを用いた乳化剤フリーのシードエマルション重合で,PTFE含有率を5.5~25.9%に変化させたPTFE/PMMAコアシェルナノ粒子を調製した。200~360°Cの加熱-冷却プロセスでPTFEは310°Cと270°Cの二重分別結晶化挙動を示した。高温(330~370°C)アニーリングで,PMMAシェル流動化によりナノコンポジットのPTFEコアは完全に分散し,強い過冷却条件下(270°C)での均一核形成による一個の結晶化発熱のみを示した。高温・長時間熱処理ではPMMAシェルの部分的分解によりいくつかのコアが接触・融合し,数成分の多重結晶化プロセス(310,297,283°C)が発現した。これは相違した結晶核形成機構によるもので,高温・長時間の熱分解でPMMA含有量が低下すると,中程度過冷却条件下(310°C)でもっとも効率的な,不均一核誘起結晶化が起こった。

シソーラス用語： *ポリテトラフルオロエチレン ,  *ポリメタクリル酸メチル ,  シード重合 ,  示差走査熱量測定 ,  *晶出温度 ,  熱分解 ,  熱サイクル ,  モルフォロジー ,  コアシェル構造
準シソーラス用語： PMMA ,  PTFE ,  アニーリング ,  タッピングモードAFM ,  *ナノコンポジット ,  加熱サイクル ,  結晶化温度