文献

J-GLOBAL ID：201002283436095664   整理番号：10A0450081

銅基板上へのレーザレーザクラッディングNi-Co二重被覆

Laser cladding Ni-Co duplex coating on copper substrate

著者 (6件)： LIU Fang (School of Materials Sci. and Engineering, Dalian Jiaotong Univ., Dalian 116028, CHN) ,  LIU Changsheng (Key Lab. for Anisotropy and Texture of Materials, Ministry of Education, Northeastern Univ., Shenyang 110004, CHN) ,  CHEN Suiyuan (Key Lab. for Anisotropy and Texture of Materials, Ministry of Education, Northeastern Univ., Shenyang 110004, CHN) ,  TAO Xingqi (Key Lab. for Anisotropy and Texture of Materials, Ministry of Education, Northeastern Univ., Shenyang 110004, CHN) ,  TAO Xingqi (Shenyang Dalu Laser Complete Equipment Co., Ltd, Shenyang 110036, CHN) ,  ZHANG Yong (School of Materials Sci. and Engineering, Dalian Jiaotong Univ., Dalian 116028, CHN)
資料名： Optics and Lasers in Engineering  (Optics and Lasers in Engineering)
巻： 48  号： 7-8  ページ： 792-799  発行年： 2010年07月 
JST資料番号： A0602B  ISSN： 0143-8166  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Ni-Co二重被覆が,連続発振CO₂レーザによって銅基板の上に成功裏にクラッドされた。クラッドした被覆の微小硬さの平均は,635HV_0.05で,これは銅基板(92HV_0.05)の約7倍であった。60分間の滑り摩耗テストにおいて,銅基板の体積損失はNi-Co二重被覆の約7倍であった。微小硬さが大きく,亀裂がないというNi-Co二重被覆の利点は,銅基板の塑性変形と凝着摩耗を減少させるのに好適で,磨耗特性の改善をもたらした。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *レーザクラッディング ,  滑り摩耗 ,  *ニッケル ,  *コバルト ,  銅 ,  炭酸ガスレーザ ,  微小硬さ ,  摩耗試験 ,  塑性変形 ,  摩耗 ,  電子顕微鏡観察 ,  被覆
準シソーラス用語： 凝着摩耗

分類 (2件)： 肉盛  (WC07060N) ,  機械的性質  (WB02030U)