低温でのガラスファイバー強化PEEK複合材料の機械的および熱膨張性質

Mechanical and thermal expansion properties of glass fibers reinforced PEEK composites at cryogenic temperatures

著者 (8件)： CHU X.x. (The Key Lab. of Cryogenics, Technical Inst. of Physics and Chemistry, Chinese Acad. of Sciences, Beijing 100190, CHN) ,  CHU X.x. (Graduate Univ. of Chinese Acad. of Sciences, Beijing 100039, CHN) ,  WU Z.x. (The Key Lab. of Cryogenics, Technical Inst. of Physics and Chemistry, Chinese Acad. of Sciences, Beijing 100190, CHN) ,  WU Z.x. (Graduate Univ. of Chinese Acad. of Sciences, Beijing 100039, CHN) ,  HUANG R.j. (The Key Lab. of Cryogenics, Technical Inst. of Physics and Chemistry, Chinese Acad. of Sciences, Beijing 100190, CHN) ,  HUANG R.j. (Graduate Univ. of Chinese Acad. of Sciences, Beijing 100039, CHN) ,  ZHOU Y. (The Key Lab. of Cryogenics, Technical Inst. of Physics and Chemistry, Chinese Acad. of Sciences, Beijing 100190, CHN) ,  LI L.f. (The Key Lab. of Cryogenics, Technical Inst. of Physics and Chemistry, Chinese Acad. of Sciences, Beijing 100190, CHN)
資料名： Cryogenics  (Cryogenics)
巻： 50  号： 2  ページ： 84-88  発行年： 2010年02月 
JST資料番号： D0115B  ISSN： 0011-2275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ポリエーテルエーテルケトン(PEEK)は高性能複合材料に対する母材として広く使用されている。本論文では,注入成型により30%切断ガラスファイバー強化PEEK複合材料を調製し,次いで異なる温度で引張り,曲げおよび衝撃性質を試験した。室温,77Kそして20Kでのガラスファイバー強化PEEKの係数,強度および比延伸を比較した。そして走査型電子顕微鏡法(SEM)により異なる試料の破壊形態を調べた。結果は,ガラスファイバー強化PEEK複合材料の機械的性質の温度依存性を示した。77Kから室温まで充填されてないPEEKとガラスファイバー強化PEEKの熱膨張係数も調べた。結果は,この温度範囲ではPEEK母材の熱膨張係数(CTE)がほぼ定数であることを示し,CTEはガラスファイバーを添加することで有意に減少させることができる。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ポリエーテルエーテルケトン ,  *ガラス繊維 ,  *繊維強化プラスチック ,  *射出成形 ,  引張試験 ,  剪断試験 ,  衝撃強さ ,  走査電子顕微鏡 ,  *熱膨張 ,  *機械的強度
準シソーラス用語： 注入成形 ,  曲げ剪断試験

分類 (1件)： 高分子固体の力学的性質  (CG02023D)

タイトルに関連する用語 (6件)： 低温 ,  ガラス ,  ファイバー強化 ,  PEEK ,  複合材料 ,  熱膨張性