Nbマイクロアロイド先進超高強度鋼における焼入-パーティショニング-焼戻法後の炭化物キャラクタリゼーション

Carbide characterization in a Nb-microalloyed advanced ultrahigh strength steel after quenching-partitioning-tempering process

著者 (5件)： WANG X.d. (School of Materials Sci. and Engineering, Shanghai Jiao Tong Univ., 800 Dongchuan Road, Shanghai 200240, CHN) ,  XU W.z. (School of Materials Sci. and Engineering, Shanghai Jiao Tong Univ., 800 Dongchuan Road, Shanghai 200240, CHN) ,  GUO Z.h. (School of Materials Sci. and Engineering, Shanghai Jiao Tong Univ., 800 Dongchuan Road, Shanghai 200240, CHN) ,  WANG L. (Baosteel Res. and Dev. Technol. Center, Shanghai 201900, CHN) ,  RONG Y.h. (School of Materials Sci. and Engineering, Shanghai Jiao Tong Univ., 800 Dongchuan Road, Shanghai 200240, CHN)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 527  号： 15  ページ： 3373-3378  発行年： 2010年06月15日 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 走査型電子顕微鏡及び透過型電子顕微鏡観察に基づき,焼入-パーティショニング-焼戻処理後のNbマイクロアロイド鋼において,4種類の炭化物を同定した。一般にケイ素を含まない炭素鋼で生じる遷移ε炭化物に加えて,他の三種類の炭化ニオブ(NbC)が処理の各段階で形成された。これらは,主に凝固過程で核生成した非整合NbC介在物,焼戻処理中に生じたラスマルテンサイト中に核生成した微細NbC及び焼入前にオーステナイト中に核生成した通常の多結晶NbCである。これらの鋼における形成機構について熱力学に基づいて簡単に議論した。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *高強度鋼 ,  *焼入 ,  *マイクロアロイド鋼 ,  ニオブ含有合金 ,  *焼戻 ,  ニオブ化合物 ,  炭化物 ,  非金属介在物 ,  マルテンサイト ,  オーステナイト ,  多結晶 ,  分配 ,  熱力学 ,  凝固 ,  核形成
準シソーラス用語： ラスマルテンサイト ,  *焼入-パーティショニング-焼戻法 ,  炭化ニオブ ,  *超高強度鋼