Sr_0.6K_0.4Fe₂As₂の微細構造及び超伝導特性に対する加熱条件の影響

Effects of heating conditions on the microstructure and superconducting properties of Sr_0.6K_0.4Fe₂As₂

著者 (7件)： ZHANG Zhiyu (Inst. of Electrical Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  QI Yanpeng (Inst. of Electrical Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  WANG Lei (Inst. of Electrical Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  GAO Zhaoshun (Inst. of Electrical Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  WANG Dongliang (Inst. of Electrical Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  ZHANG Xianping (Inst. of Electrical Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  MA Yanwei (Inst. of Electrical Engineering, Chinese Acad. of Sci., Beijing, CHN)
資料名： Superconductor Science and Technology  (Superconductor Science and Technology)
巻： 23  号： 6  ページ： 065009,1-4  発行年： 2010年06月 
JST資料番号： T0607A  ISSN： 0953-2048  CODEN： SUSTEF  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 線状のSr_0.6K_0.4Fe₂As₂多結晶バルク試料をワンステップ固相反応法により作製した。Sr,Fe,As及びKのストイキオメトリックな混合物をアルゴン雰囲気中でボールミルした。ミル及び焼結の間の元素の喪失を補うためにAs及びKを10%余分に付加した。原料粉末をNbチューブに入れ,最後に熱処理を700~900°Cで行った。試料の酸化を抑えるために熱処理の間アルゴンを流した。相の同定はX線回折により行った。抵抗及び磁化測定は7Tまでの磁場中で行った。磁気臨界電流密度はBeanモデルを使用して計算した。微細構造は走査電子顕微鏡により観察した。アニール温度は臨界転移温度T_c以外の超伝導特性に影響した。850°C以上で焼結すると不純物相は消え,最良の臨界電流密度J_cが得られた。不純物相が超伝導特性を左右する重要な因子であることが分かった。