α-Fe₂O₃ナノチューブの調製のための水熱法と過塩素酸アンモニウムの熱分解のためのその触媒性能

A hydrothermal method for preparation of α-Fe₂O₃ nanotubes and their catalytic performance for thermal decomposition of ammonium perchlorate

著者 (5件)： SONG Limin (Coll. of Environment and Chemical Engineering & Tianjin Key Lab. of Fiber Modification and Functional Fiber, Tianjin ...) ,  ZHANG Shujuan (Coll. of Sci., Tianjin Univ. of Sci. & Technol., Tianjin 300457, CHN) ,  CHEN Bin (Coll. of Environment and Chemical Engineering & Tianjin Key Lab. of Fiber Modification and Functional Fiber, Tianjin ...) ,  GE Jingjie (Coll. of Environment and Chemical Engineering & Tianjin Key Lab. of Fiber Modification and Functional Fiber, Tianjin ...) ,  JIA Xicheng (Coll. of Environment and Chemical Engineering & Tianjin Key Lab. of Fiber Modification and Functional Fiber, Tianjin ...)
資料名： Colloids and Surfaces. A. Physicochemical and Engineering Aspects  (Colloids and Surfaces. A. Physicochemical and Engineering Aspects)
巻： 360  号： 1-3  ページ： 1-5  発行年： 2010年05月05日 
JST資料番号： A0539B  ISSN： 0927-7757  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 界面活性剤もテンプレートも必要としないα-Fe₂O₃ナノチューブ調製のための水熱法について述べた。調製した粉体の結晶構造とモルフォロジーを粉末X線回折,Fourier変換赤外分光法,及び透過型電子顕微鏡を用いて調べた。その結果,高結晶性α-Fe₂O₃ナノチューブの平均長さ,直径,及び壁厚はそれぞれ,約200~1000nm,100~150nm,及び25~30nmであることが分かった。α-Fe₂O₃ナノチューブを低温で過塩素酸アンモニウムの熱分解用触媒として用いた。α-Fe₂O₃ナノチューブ上での過塩素酸アンモニウムの分解の詳細な反応機構を提案した。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *酸化鉄 ,  *ナノチューブ ,  *水熱合成 ,  *過塩素酸アンモニウム ,  *熱分解 ,  *触媒活性 ,  界面活性剤 ,  型 ,  結晶構造 ,  モルフォロジー ,  X線回折 ,  赤外吸収スペクトル ,  透過型電子顕微鏡 ,  結晶度 ,  長さ ,  直径 ,  壁面 ,  厚み ,  反応機構 ,  示差走査熱量測定
準シソーラス用語： DSC【熱量測定】 ,  FTIRスペクトル ,  テンプレート【型】 ,  管壁 ,  結晶性 ,  厚さ ,  粉末X線回折

分類 (3件)： 塩基,金属酸化物  (CD01030Z) ,  金属酸化物及び金属カルコゲン化物の結晶構造  (BK07020Y) ,  不均一系触媒反応  (CB06100E)

タイトルに関連する用語 (6件)： ナノチューブ ,  調製 ,  水熱法 ,  過塩素酸アンモニウム ,  熱分解 ,  触媒性能