(傾斜)(Ti,Al)Nコーティングした1Cr11Ni2W2MoVステンレス鋼の高温での疲れ挙動

Fatigue behavior of (graded) (Ti, Al)N-coated 1Cr11Ni2W2MoV stainless steel at high temperature

著者 (5件)： XIN Li (State key Lab. for Corrosion and Protection of Metals, Inst. of Metal Res., Chinese Acad. of Sciences, Wencui Road ...) ,  LIU Ping (State key Lab. for Corrosion and Protection of Metals, Inst. of Metal Res., Chinese Acad. of Sciences, Wencui Road ...) ,  FENG Changjie (School of Materials Sci. and Engineering, Nanchang Hangkong Univ., Nanchang, 330063, CHN) ,  ZHU Shenglong (State key Lab. for Corrosion and Protection of Metals, Inst. of Metal Res., Chinese Acad. of Sciences, Wencui Road ...) ,  WANG Fuhui (State key Lab. for Corrosion and Protection of Metals, Inst. of Metal Res., Chinese Acad. of Sciences, Wencui Road ...)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 204  号： 15  ページ： 2417-2423  発行年： 2010年04月25日 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 回転曲げ疲れ試験機を用いて,500°Cでの傾斜(Ti,Al)N-及びTi_0.7Al_0.3Nを被覆した1Cr11Ni2W2MoVの高サイクル疲れ特性を調べた。その結果,1Cr11Ni2W2MoVステンレス鋼の疲れ強さ及び寿命は,Ti_0.7Al_0.3Nコーティングが存在することによって明らかに増加することが判る。高応力レベル(475MPa~525MPa)で傾斜コーティングが存在することによって疲れ寿命及び強さもある程度改善した。SEMで破断形態を解析した。良く固着した高圧縮応力のコーティングが存在することは,基板の塑性変形を抑制し,したがって鋼の疲れ特性を改善したと結論づけた。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ステンレス鋼 ,  *窒化物 ,  *チタン化合物 ,  *アルミニウム化合物 ,  *高温疲れ ,  高サイクル疲れ ,  疲れ強さ ,  疲れ寿命 ,  圧縮応力 ,  基板 ,  塑性変形 ,  *セラミック被覆 ,  傾斜機能材料 ,  クロム含有合金 ,  ニッケル含有合金 ,  タングステン含有合金 ,  モリブデン含有合金 ,  バナジウム含有合金