炭化タンタルのスパークプラズマ焼結

Spark plasma sintering of tantalum carbide

著者 (6件)： KHALEGHI Evan (Dep. of Mechanical Engineering, San Diego State Univ., 5500 Campanile Dr., San Diego, CA 92182-1323, USA) ,  KHALEGHI Evan (Dep. of Mechanical and Aerospace Engineering, Univ. of California, San Diego, 9500 Gilman Drive, La Jolla, CA 92093, USA) ,  LIN Yen-shan (Dep. of Mechanical Engineering, San Diego State Univ., 5500 Campanile Dr., San Diego, CA 92182-1323, USA) ,  LIN Yen-shan (Dep. of Mechanical and Aerospace Engineering, Univ. of California, San Diego, 9500 Gilman Drive, La Jolla, CA 92093, USA) ,  MEYERS Marc A. (Dep. of Mechanical and Aerospace Engineering, Univ. of California, San Diego, 9500 Gilman Drive, La Jolla, CA 92093, USA) ,  OLEVSKY Eugene A. (Dep. of Mechanical Engineering, San Diego State Univ., 5500 Campanile Dr., San Diego, CA 92182-1323, USA)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 63  号： 6  ページ： 577-580  発行年： 2010年09月 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： スパークプラズマ焼結により炭化タンタル粉末を焼結した。試料を種々の温度及び圧力条件の下で処理,その性質を相対密度,結晶粒度,破壊強度および硬度により特徴付けた。結果を同じ条件にて実施したホットプレスのそれらと比較した。その結果,緻密化は実質的に結晶成長を伴っている。結晶成長を抑制するためにカーボンナノチューブを添加したが,試料の破壊強度および最終密度が増加した一方で,結晶成長にはほとんど効果がなかった。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *炭化タンタル ,  *放電焼結 ,  緻密化 ,  相対密度 ,  *結晶粒度 ,  破壊強さ ,  硬度 ,  *結晶成長 ,  カーボンナノチューブ ,  添加物効果 ,  セラミック ,  *放電プラズマ焼結
準シソーラス用語： *スパークプラズマ焼結

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (2件)： 炭化タンタル ,  スパークプラズマ焼結