アルカリ溶液中の化学脱合金によるモノリシックナノ多孔性銅形成に対する初期Al-Cu合金の相成分と比率の影響

Influence of phase constituent and proportion in initial Al-Cu alloys on formation of monolithic nanoporous copper through chemical dealloying in an alkaline solution

著者 (6件)： LIU W.b. (School of Manufacturing Sci. and Engineering, Sichuan Univ., Chengdu 610065, CHN) ,  LIU W.b. (School of Materials Sci. and Engineering, Beijing Univ. of Aeronautics and Astronautics, Beijing 100191, CHN) ,  ZHANG S.c. (School of Materials Sci. and Engineering, Beijing Univ. of Aeronautics and Astronautics, Beijing 100191, CHN) ,  LI N. (School of Manufacturing Sci. and Engineering, Sichuan Univ., Chengdu 610065, CHN) ,  ZHENG J.w. (School of Materials Sci. and Engineering, Beijing Univ. of Aeronautics and Astronautics, Beijing 100191, CHN) ,  XING Y.l. (School of Materials Sci. and Engineering, Beijing Univ. of Aeronautics and Astronautics, Beijing 100191, CHN)
資料名： Corrosion Science  (Corrosion Science)
巻： 53  号： 2  ページ： 809-814  発行年： 2011年02月 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： アルカリ溶媒を用いて33~50at.%Cu含有の融解紡糸Al-Cu合金を化学脱合金することによりモノリシックナノ多孔性銅(NPC)リボンを製造した。結果からNPC形成に対して初期合金の相成分と比率は重要な影響を持っていることがわかる。初期合金中にAlCuが存在しないか又は僅かである場合にのみ,単独又はAl₂CuとAlCuの組合わせから成る合金リボンをアルカリ溶液で完全に脱合金することができる。さらにNPC中の靭帯/孔の長さ規模は初期合金中のAlCu量を単純に変化させることによって広い範囲で調整することが可能である。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *銅合金 ,  アルミニウム添加合金 ,  *脱金属 ,  *多孔質金属 ,  *銅 ,  溶融紡糸 ,  リボン ,  混合比 ,  ナノ構造
準シソーラス用語： 脱合金

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (10件)： アルカリ溶液 ,  化学 ,  脱合金 ,  ナノ多孔性 ,  銅 ,  初期 ,  Al ,  Cu合金 ,  相成分 ,  比率