レーザ急速成形インコネル718ニッケル系超合金の微細構造と残留応力

Microstructure and residual stress of laser rapid formed Inconel 718 nickel-base superalloy

著者 (6件)： LIU Fencheng (State Key Lab. of Solidification Processing, Northwestern Polytechnical Univ., Xi’an 710072, CHN) ,  LIN Xin (State Key Lab. of Solidification Processing, Northwestern Polytechnical Univ., Xi’an 710072, CHN) ,  YANG Gaolin (State Key Lab. of Solidification Processing, Northwestern Polytechnical Univ., Xi’an 710072, CHN) ,  SONG Menghua (State Key Lab. of Solidification Processing, Northwestern Polytechnical Univ., Xi’an 710072, CHN) ,  CHEN Jing (State Key Lab. of Solidification Processing, Northwestern Polytechnical Univ., Xi’an 710072, CHN) ,  HUANG Weidong (State Key Lab. of Solidification Processing, Northwestern Polytechnical Univ., Xi’an 710072, CHN)
資料名： Optics & Laser Technology  (Optics & Laser Technology)
巻： 43  号： 1  ページ： 208-213  発行年： 2011年02月 
JST資料番号： D0245B  ISSN： 0030-3992  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： レーザ急速成形(LRFed)ニッケル系超合金インコネル718の微細構造と残留応力を調査した。LRFedインコネル718合金の堆積された微細構造は,堆積方向に沿ってエピタキシャル成長する柱状の樹枝状結晶と高温での焼きなまし処理後の不規則に分布した等軸結晶粒に変換された柱状の樹枝状結晶からなる。Vickersマイクロインデンテーション法による微細構造のスケールの残留応力評価は,残留熱応力がLRFed試料中に不規則に分布し,溶液焼きなまし処理の間の再結晶化に重大な影響を及ぼすことを示す。レーザ急速成形の間の急速加熱と冷却により残留応力が導かれる。単一堆積層内の高残留応力領域と低残留応力領域の間に交互分布が存在するので,再結晶した結晶粒のサイズの同様の分布を生じる。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： インコネル ,  残留応力 ,  微細構造 ,  *レーザ加工 ,  ニッケル合金 ,  クロム含有合金 ,  鉄含有合金 ,  モリブデン含有合金 ,  ニオブ含有合金 ,  チタン含有合金 ,  エピタクシー ,  樹枝状結晶 ,  硬さ試験 ,  *特殊成形 ,  レーザ応用
準シソーラス用語： Inconel718 ,  マイクロインデンテーション ,  *レーザ成形