イソタクチックポリプロピレンの部分融解と再結晶化

PARTIAL MELTING AND RECRYSTALLIZATION OF ISOTACTIC POLYPROPYLENE

著者 (6件)： Tian-nan Zhou (Dep. of Polymer Sci. and Materials,Sichuan Univ. State Key Lab. of Polyreer Materials Engineering, Sichuan, Chengdu) ,  Hong Yang (Dep. of Polymer Sci. and Materials,Sichuan Univ. State Key Lab. of Polyreer Materials Engineering, Sichuan, Chengdu) ,  Nan-ying Ning (Dep. of Polymer Sci. and Materials,Sichuan Univ. State Key Lab. of Polyreer Materials Engineering, Sichuan, Chengdu) ,  Yu-fang Xiang (Dep. of Polymer Sci. and Materials,Sichuan Univ. State Key Lab. of Polyreer Materials Engineering, Sichuan, Chengdu) ,  Rong-ni Du (Dep. of Polymer Sci. and Materials,Sichuan Univ. State Key Lab. of Polyreer Materials Engineering, Sichuan, Chengdu) ,  Qiang Fu (Dep. of Polymer Sci. and Materials,Sichuan Univ. State Key Lab. of Polyreer Materials Engineering, Sichuan, Chengdu)
資料名： Chinese Journal of Polymer Science  (Chinese Journal of Polymer Science)
巻： 28  号： 1  ページ： 77-83  発行年： 2010年 
JST資料番号： C2566A  ISSN： 0256-7679  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： シンガポール (SGP)  言語： 英語 (EN)

抄録/ポイント： 相対的に高い結晶化温度(135°C)を選定してイソタクチックポリプロピレン(iPP)球晶を充分に成長させ,次いで,165°Cで部分融解させた。その温度では形成球晶サイズのみが減少し,完全融解はしなかった。この部分融解iPPの結晶化挙動を示差走査熱量測定(DSC)と偏光顕微鏡(PLM)により注意深く調べた。その結果,特異的アニール温度(165°C)でのiPPの融解挙動には異なる機構に基づいた2種の部分が含まれ,1種はiPP球晶外面の融解で,もう1種は長いアニール時間での非融解球晶の部分的ラメラ完全化であった。iPP融液の立体配座秩序はアニール温度の増加により低下した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *イソタクチックポリプロピレン ,  部分融解 ,  再結晶 ,  晶出温度 ,  立体配座 ,  焼なまし ,  結晶化 ,  示差走査熱量測定 ,  偏光顕微鏡
準シソーラス用語： 再結晶化 ,  結晶化温度 ,  アニール

分類 (1件)： 高分子化学一般  (CG01000B)

タイトルに関連する用語 (3件)： イソタクチックポリプロピレン ,  部分融解 ,  再結晶化