溶融紡糸を用いて合成したZrNiSnベースの半Heusler熱電材料の微細構造

Microstructure of ZrNiSn-base Half-Heusler Thermoelectric Materials Prepared by Melt-spinning

著者 (7件)： Yu Cui (State Key Lab. of Silicon Materials, Dep. of Materials Sci. and Engineering, Zhejiang Univ., Hangzhou) ,  Zhu Tiejun (State Key Lab. of Silicon Materials, Dep. of Materials Sci. and Engineering, Zhejiang Univ., Hangzhou) ,  Xiao Kai (State Key Lab. of Silicon Materials, Dep. of Materials Sci. and Engineering, Zhejiang Univ., Hangzhou) ,  Jin Ji (State Key Lab. of Silicon Materials, Dep. of Materials Sci. and Engineering, Zhejiang Univ., Hangzhou) ,  Shen Junjie (State Key Lab. of Silicon Materials, Dep. of Materials Sci. and Engineering, Zhejiang Univ., Hangzhou) ,  Yang Shenghui (State Key Lab. of Silicon Materials, Dep. of Materials Sci. and Engineering, Zhejiang Univ., Hangzhou) ,  Zhao Xinbing (State Key Lab. of Silicon Materials, Dep. of Materials Sci. and Engineering, Zhejiang Univ., Hangzhou)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 25  号： 6  ページ： 569-572  発行年： 2010年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 熱電材料のZr(Hf)NiSn(Sb)合金を,微細構造をリファインするために,レビテーション溶融と次いでの溶融紡糸によって合成し,特性を測定するために放電プラズマ焼結を用いて固化した。XRD解析によって,半Heusler相が生成することが判明した。溶融紡糸した薄いリボンの微細構造を,走査電子顕微鏡及び透過電子顕微鏡を用いて研究した。この薄いリボンはサイズが数百ナノメータで,焼結プロセスではそれ以上に成長しなかった。結晶顆粒中にナノ結晶が見出された。レビテーション溶融サンプルに比べて,溶融紡糸サンプルに対するキャリア濃度は増加し,ナノ結晶は金属性であることが判明した。溶融紡糸による界面散乱の増加は,格子熱伝導率を低下させた。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 溶融紡糸 ,  *熱電材料 ,  微細構造 ,  合金 ,  レビテーション溶融 ,  放電焼結 ,  走査電子顕微鏡 ,  透過型電子顕微鏡 ,  キャリア密度 ,  ナノ結晶 ,  熱伝導率 ,  放電プラズマ焼結
準シソーラス用語： 透過電子顕微鏡 ,  キャリア濃度 ,  格子熱伝導率