高温水中の冷間圧延316NGステンレス鋼の応力腐食割れに対する水化学と負荷条件の影響

Effects of water chemistry and loading conditions on stress corrosion cracking of cold-rolled 316NG stainless steel in high temperature water

著者 (6件)： LU Zhanpeng (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba 6-6-01, Sendai 980-8579, JPN) ,  SHOJI Tetsuo (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba 6-6-01, Sendai 980-8579, JPN) ,  MENG Fanjiang (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba 6-6-01, Sendai 980-8579, JPN) ,  QIU Yubing (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba 6-6-01, Sendai 980-8579, JPN) ,  DAN Tichun (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba 6-6-01, Sendai 980-8579, JPN) ,  XUE He (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba 6-6-01, Sendai 980-8579, JPN)
資料名： Corrosion Science  (Corrosion Science)
巻： 53  号： 1  ページ： 247-262  発行年： 2011年01月 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 288°Cの純水中で冷間圧延316NGステンレス鋼の応力腐食割れ成長に対する電極電位,応力強度と負荷履歴の影響を研究した。ランダムな結晶粒界に沿った亀裂分枝と粒間応力腐食割れを電子後方散乱回折によって観察した。亀裂成長速度は応力拡大係数に対して強い依存性があることがわかる。1周期の過負荷により遅れ過渡亀裂成長周期が生じた。冷間圧延316NGSSの亀裂成長に対する電極電位減少のマイルドな抑制効果を亀裂先端力学と亀裂先端酸化速度間の相互作用をベースとして解析する。Copyright 2010 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *応力腐食割れ ,  *ステンレス鋼 ,  高温水 ,  冷延鋼板 ,  粒界割れ ,  成長速度 ,  応力拡大係数 ,  電極電位 ,  亀裂伝搬 ,  亀裂先端 ,  *応力 ,  *水化学 ,  *亀裂 ,  *腐食割れ

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (5件)： 高温水 ,  冷間圧延 ,  ステンレス鋼 ,  応力腐食割れ ,  水化学