グラフェンナノシート/スチレン-アクリル乳濁液ハイブリッド導電膜の調製

Preparation of Graphene Nanosheets/Styrene-Acrylic Emulsion Hybrid Conductive Film

著者 (6件)： Yang Bo (Res. Instiute of Hybrid Materials, The Preliminary State Key Lab. of Fiber and Textile Materials, Shandong, Qingdao) ,  Tang Jianguo (Res. Instiute of Hybrid Materials, The Preliminary State Key Lab. of Fiber and Textile Materials, Shandong, Qingdao) ,  Liu Jixian (Res. Instiute of Hybrid Materials, The Preliminary State Key Lab. of Fiber and Textile Materials, Shandong, Qingdao) ,  Wang Yao (Res. Instiute of Hybrid Materials, The Preliminary State Key Lab. of Fiber and Textile Materials, Shandong, Qingdao) ,  Dong Menglong (Res. Instiute of Hybrid Materials, The Preliminary State Key Lab. of Fiber and Textile Materials, Shandong, Qingdao) ,  Niu Lin (Res. Instiute of Hybrid Materials, The Preliminary State Key Lab. of Fiber and Textile Materials, Shandong, Qingdao)
資料名： Tuliao Gongye  (Tuliao Gongye)
巻： 40  号： 9  ページ： 5-8  発行年： 2010年 
JST資料番号： C2486A  ISSN： 0253-4312  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： グラフェンナノシートを,導電性充填材料に選び,一種の新規ハイブリッド導電膜を作るために,スチレン-アクリル乳濁液と物理的に混合した。原料およびハイブリッド導電膜のモルフォロジーおよび構造を特性評価した。ハイブリッド導電膜の導電性の性能および機構を,予備的に研究した。結果から,グラフェンナノシートがポリマーマトリックス内に均一に分散し,グラフェンの質量画分が5%であったとき,表面抵抗は0.29Ωcmであることが明らかになった。しかし,グラフェンの凝集が出現し,表面抵抗はグラフェンの含量の増加とともにかなり上昇した。電気伝導率は,少量のナノ銀をハイブリッド導電膜に添加すると2桁上昇するであろう。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 単一層 ,  *グラファイト ,  ナノ構造 ,  膜 ,  乳濁液 ,  乳化型液膜 ,  *薄膜 ,  充填剤 ,  表面抵抗 ,  電気伝導率 ,  ナノ粒子 ,  グラフェン ,  *ナノシート
準シソーラス用語： グラフェンシート ,  銀ナノ粒子 ,  導電性充填剤 ,  *導電膜

分類 (3件)： その他の無機化合物の薄膜  (BK14060A) ,  有機化合物の薄膜  (BK14070L) ,  高分子固体の物理的性質  (CG02024U)

タイトルに関連する用語 (6件)： グラフェンナノシート ,  スチレン ,  アクリル ,  乳濁液 ,  導電膜 ,  調製