ポリエチレングリコールジメタクリレートの光開始RAFT架橋重合

PHOTOINITIATED RAFT CROSSLINKING POLYMERIZATION OF POLYETHYLENE GLYCOL DIMETHACRYLATES

著者 (6件)： Zhuo Ding (State Key Lab. of Polymer Materials Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Chen Zhi (State Key Lab. of Polymer Materials Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Wang Xiaolong (State Key Lab. of Polymer Materials Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Ruan Yingbo (State Key Lab. of Polymer Materials Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Zhao Xuemei (State Key Lab. of Polymer Materials Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu) ,  Ran Rong (State Key Lab. of Polymer Materials Engineering, Coll. of Polymer Sci. and Engineering, Sichuan Univ., Chengdu)
資料名： Gaofenzi Xuebao  (Gaofenzi Xuebao)
号： 5  ページ： 561-566  発行年： 2010年 
JST資料番号： W0847A  ISSN： 1000-3304  CODEN： GAXUE9  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 可逆的付加-フラグメンテーション連鎖移動(RAFT)剤のS-1-ドデシル-S′-(α,α′-ジメチル-α′′-酢酸)トリチオカーボネートを合成した。ポリエチレングリコールジメタクリレート(PEGDMA)の室温でのUV開始RAFT重合挙動を示差走査光熱量測定(DPC)と動的機械分析(DMA)により調べた。RAFT系の光重合速度は通常ラジカル重合よりも著しく低く,付加反応が拡散律速になるに従って穏やかな自己促進が生じた。RAFT重合速度と最終転化率に及ぼすメタクリレート基間スペーサ距離の影響も調べた。その結果,メタクリレート基間エチレングリコール単位数の増加と共に最終転化率が徐々に増加し,重合速度は最初減少した後に増加に転じた。3種のPEGDMAsの比較から,より長い中央セグメントをもつPEGDMAがより均一なネットワークと低い架橋度を与えた。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： ポリエチレングリコールジメタクリレート ,  *架橋重合 ,  連鎖移動 ,  リビングラジカル重合 ,  光重合 ,  付加反応 ,  架橋度 ,  反応速度
準シソーラス用語： 可逆的付加-フラグメンテーション連鎖移動 ,  RAFT重合 ,  重合速度