動的充填射出成形により得られるPA1010/PPブレンドのモルホロジーと機械特性

MORPHOLOGY AND MECHANICAL PROPERTIES OF PA1010/PP BLENDS OBTAINED VIA DYNAMIC PACKING INJECTION MOLDING

著者 (7件)： Yang Fengxia (Coll. of Polymer Sci. and Engineering, State Key Lab. of Polymer Engineering, Sichuan Univ., Chengdu) ,  Zhou Chengjuan (Coll. of Polymer Sci. and Engineering, State Key Lab. of Polymer Engineering, Sichuan Univ., Chengdu) ,  Du Rongni (Coll. of Polymer Sci. and Engineering, State Key Lab. of Polymer Engineering, Sichuan Univ., Chengdu) ,  Yang Jinghui (Coll. of Polymer Sci. and Engineering, State Key Lab. of Polymer Engineering, Sichuan Univ., Chengdu) ,  Fu Qiang (Coll. of Polymer Sci. and Engineering, State Key Lab. of Polymer Engineering, Sichuan Univ., Chengdu) ,  Su Run (Coll. of Polymer Sci. and Engineering, State Key Lab. of Polymer Engineering, Sichuan Univ., Chengdu) ,  Zhang Qin (Coll. of Polymer Sci. and Engineering, State Key Lab. of Polymer Engineering, Sichuan Univ., Chengdu)
資料名： Gaofenzi Xuebao  (Gaofenzi Xuebao)
号： 7  ページ： 849-856  発行年： 2010年 
JST資料番号： W0847A  ISSN： 1000-3304  CODEN： GAXUE9  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 非相溶PA1010/PPブレンドの機械特性に及ぼす相モルホロジーの影響を動的充填射出成形(DPIM)により調べた。せん断負荷により引張強さ,引張弾性率,ノッチ付衝撃強さが著しく増加し,PP含量が20%のときの動的試料のIzod衝撃強さは21.3kJ/m,引張強さは50.9MPaで,これらの値はそれぞれ静的試料の3倍以上と1.5倍であった。SEM結果から,中心にコア,コア周りにせん断層をもつせん断誘起モルホロジーが試験片断面に認められた。EM結果からは,動的成形試験片でのドメインサイズの著しい低下とより均一な分散性が示され,特に,PP含量が20%ではドメインサイズが約3.9μmから約1.4μmに低下した。動的試料の高い機械特性はせん断応力下での相モルホロジー効果に起因した。DPIMに基づくせん断応力誘起分子配向により,動的試料の引張強さは全組成範囲で静的試料よりも高く,その強靭化機構はせん断誘起のドメインサイズ微細化と分子配向に由来した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 射出成形 ,  *ポリマブレンド ,  モルフォロジー ,  機械的性質 ,  剪断 ,  引張強さ ,  弾性係数 ,  衝撃強さ
準シソーラス用語： *ブレンドポリマ ,  機械特性 ,  引張弾性率