隣接架橋ポリウレタン-尿素エラストマの合成と耐熱性

Preparation and Heat-Resistance of the Adjacency Crosslinked Polyurethane-Urea Elastomers

著者 (5件)： Li Zaifeng (Key Lab. of Eco-Chemical Engineering, Ministry of Education, Coll. of Chemistry and Molecular Engineering, Qingdao ...) ,  Sun Jian (Key Lab. of Eco-Chemical Engineering, Ministry of Education, Coll. of Chemistry and Molecular Engineering, Qingdao ...) ,  Wang Shengjun (Key Lab. of Eco-Chemical Engineering, Ministry of Education, Coll. of Chemistry and Molecular Engineering, Qingdao ...) ,  Du Juan (Key Lab. of Eco-Chemical Engineering, Ministry of Education, Coll. of Chemistry and Molecular Engineering, Qingdao ...) ,  Wang Zenglin (Key Lab. of Eco-Chemical Engineering, Ministry of Education, Coll. of Chemistry and Molecular Engineering, Qingdao ...)
資料名： Gaofenzi Cailiao Kexue yu Gongcheng  (Gaofenzi Cailiao Kexue yu Gongcheng)
巻： 26  号： 7  ページ： 140-142,146  発行年： 2010年 
JST資料番号： C2119A  ISSN： 1000-7555  CODEN： GCKGEI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ソフトセグメントにポリブタジエン-アクリロニトリル共重合体グリコール(HTBN)とポリテトラヒドロフラングリコール(PTHF)の混合物,ハードセグメントにトルエンジイソシアナート(TDI),鎖延長剤にジメチルチオトルエンジアミン(DMTDA),架橋剤にB25及びHAV-2を用いて,隣接架橋ポリウレタン-尿素(PUU)エラストマを合成した。軟化点試験から,B25及びHAV-2の共架橋効果により架橋PUUはその軟化点が消失し,熱可塑性から熱硬化性に転換した。歪-応力挙動から,架橋PUUの機械特性は線状PUUよりも低下したが,熱重量分析からは熱安定性が著しく改良された。温度増加と共に架橋PUUの高温機械特性と破断伸びが低下し,硬度は漸減したが,弾力性は増加した。B25含量の増加により架橋PUUの100°C又は150°Cでの機械特性保持率(σh/σl)が増加した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 架橋【高分子】 ,  ポリウレタン ,  *ゴム ,  耐熱性 ,  共重合体 ,  軟化点 ,  熱塑性 ,  熱硬化 ,  機械的性質 ,  ウレア化合物
準シソーラス用語： *エラストマ ,  熱可塑性 ,  機械特性

分類 (1件)： 高分子化学一般  (CG01000B)

物質索引 (1件)： 尿素

タイトルに関連する用語 (4件)： 架橋 ,  ポリウレタン-尿素 ,  エラストマ ,  耐熱性