Tm(3+)をドープしたTeO_2WO_3La_2O_3ガラスの熱的及び分光学的特性に及ぼすWO_3含有量の影響

Effects of WO_3 Contents on the Thermal and Spectroscopic Properties of Tm(3+) doped TeO_2 WO_3 La2O_3 Glasses

著者 (5件)： Li Kefeng (Key Lab. of Materials for High Power Laser, Shanghai Inst. of Optics and Fine Mechanics, Chinese Acad. of Sciences ...) ,  Wang Guonian (Key Lab. of Materials for High Power Laser, Shanghai Inst. of Optics and Fine Mechanics, Chinese Acad. of Sciences ...) ,  Hu Lili (Key Lab. of Materials for High Power Laser, Shanghai Inst. of Optics and Fine Mechanics, Chinese Acad. of Sciences ...) ,  Zhang Junjie (Key Lab. of Materials for High Power Laser, Shanghai Inst. of Optics and Fine Mechanics, Chinese Acad. of Sciences ...) ,  Hu Junjiang (Key Lab. of Materials for High Power Laser, Shanghai Inst. of Optics and Fine Mechanics, Chinese Acad. of Sciences ...)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 25  号： 4  ページ： 429-434  発行年： 2010年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： モル組成が(90-x)TeO_2-xWO_3-9La_2O_3-1Tm_2O_3(x=10,20,30(mol%))タングステンランタン亜テルル酸塩(TWL)ガラスを合成した。Tm(3+)をドープしたTWLガラスの熱安定性及び分光学的特性に及ぼすWO_3含有量の影響を研究した。WO_3含有量が増加するとTWLガラスの熱安定性が改良されることが判明した。30mol%のWO_3を有するガラスのガラス転移温度(Tg)は457°Cで,結晶化開始温度(Tx)はDTA曲線に於いて観察されず,ガラスの熱膨張係数は1.224×10(-5)/°C(30~300°C)に低下した。ガラスの最大フォノンエネルギーはホスト組成への依存を示した。分光学的強度パラメータ(Ωt,t=2,4,6),放射遷移速度,放射寿命,及び分岐比率をJudd-Ofelt理論を用いて計算した。Tm(3+):3F4→3H6遷移の発光断面積をMcCumber理論を用いて計算した。60TeO_2-30WO_3-9La_2O_3-1Tm_2O_3ガラスに於けるTm(3+)の最大発光断面積は9.6×10(-21)cm2であった。熱的及び分光学的特性から評価して,60TeO_2-30WO_3-10La_2O_3ガラスは2.0μmレーザに対する有望なホスト材料であった。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： ドーピング ,  *ガラス ,  含有量 ,  スペクトロスコピー ,  熱安定性 ,  理論 ,  ガラス転移点 ,  熱膨張係数 ,  断面積
準シソーラス用語： ドープ ,  分光学 ,  Judd-Ofelt理論 ,  ガラス転移温度 ,  発光断面積