塊状重合による強靭化ABS樹脂の調製と機械的性質

Preparation and Mechanical Properties of Toughened ABS Resin via Bulk Polymerization

著者 (6件)： Yu Zhixing (Dep. of Polymer Sci. and Engineering, School of Chemical Engineering, Dalian Univ. of Technology;;Liaoning Key Lab. ...) ,  Li Yang (Dep. of Polymer Sci. and Engineering, School of Chemical Engineering, Dalian Univ. of Technology;;Liaoning Key Lab. ...) ,  Wang Chaoxian (Res. Inst. of Beijing Yanshan Petrochemical Corp., SINOPEC, Beijing) ,  Wang Shaopeng (Dep. of Polymer Sci. and Engineering, School of Chemical Engineering, Dalian Univ. of Technology;;Liaoning Key Lab. ...) ,  Wang Yurong (Dep. of Polymer Sci. and Engineering, School of Chemical Engineering, Dalian Univ. of Technology;;Liaoning Key Lab. ...) ,  Song Shunxi (Dep. of Polymer Sci. and Engineering, School of Chemical Engineering, Dalian Univ. of Technol., Dalian)
資料名： Cailiao Yanjiu Xuebao  (Cailiao Yanjiu Xuebao)
巻： 24  号： 1  ページ： 55-60  発行年： 2010年 
JST資料番号： W0603A  ISSN： 1005-3093  CODEN： CYXUEV  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 一連のアクリロニトリル-ブタジエン-スチレン共重合樹脂三元共重合体(ABS)を,強靭剤としてポリブタジエンゴムを用いる塊状重合によって合成した。得られた材料の機械的性質を研究した。この結果は,高いcisゴムBR9004が残りのものよりはるかに優れた最良の強靭化効果を有して,相対的材料のIZODノッチ付き衝撃強さは,236.1J/mに達することを示して,それが低cisゴム700Aと結合されるとき,後者の包括的機械的性質は,Gaoqiao生成物(ABS8434)に相当した。材料破壊での衝撃強度,引っ張り特性および伸びは,アクリロニトリル含有量と樹脂相の分子量の増加と共に上昇した。しかしながら,引張性質はゴム分の増加と共に減少した。ゴムの含有量が20%未満であるとき,衝撃強度は急速に増強したが,しかし,20%以上のとき,ゆっくり増加した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *ABS樹脂 ,  *機械的性質 ,  塊状重合 ,  調製 ,  ブタジエンゴム ,  ポリブタジエン ,  特性 ,  ビニル化合物 ,  脂肪族ニトリル
準シソーラス用語： 引張特性