白金(111)面に成長した島状酸化鉄,FeO単層上での酸素空位クラスターの周期的配置生成

Formation of Periodic Arrays of O Vacancy Clusters on Monolayer FeO Islands Grown on Pt(111)

著者 (7件)： Ma Teng (Dalian Inst. of Chemical Physics, Chinese Acad. of Sciences State Key Lab. of Catalysis, Liaoning, Dalian) ,  Fu Qiang (Dalian Inst. of Chemical Physics, Chinese Acad. of Sciences State Key Lab. of Catalysis, Liaoning, Dalian) ,  Yao Yunxi (Dalian Inst. of Chemical Physics, Chinese Acad. of Sciences State Key Lab. of Catalysis, Liaoning, Dalian) ,  Cui Yi (Dalian Inst. of Chemical Physics, Chinese Acad. of Sciences State Key Lab. of Catalysis, Liaoning, Dalian) ,  Tan Dali (Dalian Inst. of Chemical Physics, Chinese Acad. of Sciences State Key Lab. of Catalysis, Liaoning, Dalian) ,  Zhai Runsheng (Dalian Inst. of Chemical Physics, Chinese Acad. of Sciences State Key Lab. of Catalysis, Liaoning, Dalian) ,  Bao Xinhe (Dalian Inst. of Chemical Physics, Chinese Acad. of Sciences State Key Lab. of Catalysis, Liaoning, Dalian)
資料名： Cuihua Xuebao  (Cuihua Xuebao)
巻： 31  号： 8  ページ： 1013-1018  発行年： 2010年 
JST資料番号： B0927B  ISSN： 0253-9837  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 1.1×10(-7)kPa O_2におけるアニーリングに及ぼす0.4の単層(ML)表面下の鉄を有する白金表面の構造進化を,走査型トンネル顕微鏡およびX線光電子分光法によって研究した。アニーリング気温が600のカリウムであったとき,O_2の解離吸着だけは発生した,それは,表面区域の地方再編成。を誘導した750のカリウムで,地中鉄原子は表面の上へ分離して,酸化だった。アニーリング気温が850のカリウムに増加されたとき,瑕疵の周期的配置を有するwell定義の単分子層FeO列島を形成した。瑕疵はFeO Moireunit細胞の地域(流動接触分解)を包まれる六方最密で位置されて,6つのなくなった酸素原子からなる単一酸素空格子点または多重酸素空格子点であった。単層FeO島に及ぼす周期的瑕疵の累層は,ポリテトラフルオロエチレン原型触媒に及ぼす構築活性部位への方法である場合があるData from the ScienceChina, LCAS. Translated by JST

シソーラス用語： 白金 ,  *酸化鉄 ,  クラスタ ,  単一層 ,  走査型トンネル顕微鏡 ,  X線光電子分光法 ,  温度 ,  ポリテトラフルオロエチレン ,  触媒 ,  カリウム
準シソーラス用語： 単層 ,  アニーリング温度

分類 (1件)： 塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (8件)： 白金 ,  成長 ,  島 ,  酸化鉄 ,  FeO ,  単層 ,  酸素 ,  クラスター