著者 (5件)： SINGH P S (Central Salt and Marine Chemicals Res. Inst. (Council of Scientific and Industrial Research), RO Membrane Div., 364 ...) ,  PARASHURAM K (Central Salt and Marine Chemicals Res. Inst. (Council of Scientific and Industrial Research), RO Membrane Div., 364 ...) ,  MAURYA S (Central Salt and Marine Chemicals Res. Inst. (Council of Scientific and Industrial Research), RO Membrane Div., 364 ...) ,  RAY P (Central Salt and Marine Chemicals Res. Inst. (Council of Scientific and Industrial Research), RO Membrane Div., 364 ...) ,  REDDY A V R (Central Salt and Marine Chemicals Res. Inst. (Council of Scientific and Industrial Research), RO Membrane Div., 364 ...)
資料名： Bulletin of Materials Science  (Bulletin of Materials Science)
巻： 35  号： 5  ページ： 817-822  発行年： 2012年10月 
JST資料番号： T0142A  ISSN： 0250-4707  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： インド (IND)  言語： 英語 (EN)

抄録/ポイント： 中空糸精密ろ過膜を異なる量のポリスルホン(PS),ポリビニルピロリドン(PVP)及びN,N-ジメチルホルムアミド(DMF)を含むポリマードープを用いて,溶液紡糸法により作製した。異なる寸法(外径と内径)と細孔特性を有する中空繊維を得るためにPS:PVP:DMF(w/w)=15:5:80,15:7:78及び17:8:75の紡糸原液を用いた。PVP/PS比が同じ0.47で,17wt%PS溶液よりも15wt%PS溶液から紡糸した中空糸膜が比較的高い透水性を示した。15wt%PS溶液のドープ溶液でPVP/PS比が0.33へ減少するとより低いフラックスの中空糸膜が生成した。紡糸パラメータの変化により,異なる寸法の繊維を微構造形態を大きく変えることなく得られた。PEO/BSA溶液の浸透による汚染に起因したフラックスの減少はPVP/PS比0.47で,15wt%PS溶液から作製した中空糸膜で最大となったが,17wt%PS溶液から作製した中空糸膜では汚染は僅かで定常的なフラックスが認められた。Copyright 2012 Indian Academy of Sciences Translated from English into Japanese by JST.

シソーラス用語： *ポリスルホン ,  *中空繊維 ,  *精密濾過 ,  湿式紡糸 ,  ポリビニルピロリドン ,  微細構造 ,  性能 ,  汚染 ,  透水性 ,  ポリエチレンオキシド ,  血清アルブミン ,  透過流束 ,  脂肪族カルボン酸 ,  カルボアミド
準シソーラス用語： ウシ血清アルブミン

分類 (1件)： 膜分離  (XD02120Z)

物質索引 (1件)： N,N-ジメチルホルムアミド

タイトルに関連する用語 (5件)： ポリスルホン ,  精密ろ過 ,  中空糸膜 ,  汚染 ,  研究