冷間鍛造とその後の焼鈍により処理されたマグネシウム合金の強化されたストレッチ成形性と機械的性質

Enhanced stretch formability and mechanical properties of a magnesium alloy processed by cold forging and subsequent annealing

著者 (6件)： WU Xinxing (Educational Key Lab. of Nonferrous Metal Materials Sci. and Engineering, School of Materials Sci. and Engineering ...) ,  YANG Xuyue (Educational Key Lab. of Nonferrous Metal Materials Sci. and Engineering, School of Materials Sci. and Engineering ...) ,  MA Jijun (Educational Key Lab. of Nonferrous Metal Materials Sci. and Engineering, School of Materials Sci. and Engineering ...) ,  HUO Qinghuan (Educational Key Lab. of Nonferrous Metal Materials Sci. and Engineering, School of Materials Sci. and Engineering ...) ,  WANG Jun (Educational Key Lab. of Nonferrous Metal Materials Sci. and Engineering, School of Materials Sci. and Engineering ...) ,  SUN Huan (Educational Key Lab. of Nonferrous Metal Materials Sci. and Engineering, School of Materials Sci. and Engineering ...)
資料名： Materials & Design  (Materials & Design)
巻： 43  ページ： 206-212  発行年： 2013年01月 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： マグネシウム合金AZ21を,室温で累積ひずみΣΔε=1.5に多方向鍛造し,次いで種々の焼鈍処理を施した。結果は,初期の粒が徐々に機械双晶により超微細粒に細分化されたことを示した。焼鈍温度は微細構造の進展に顕著な効果を持っていた。523Kでは,3.8μmの平均粒径を持つ均質構造が得られ,それは,焼鈍試料と比較して顕著なテクスチャ弱体化を示し,延性とストレッチ成形性の大きな増加をもたらした。焼鈍温度の上昇と下降は何れも粒径の粗大化につながる。更に,焼鈍中の再結晶速度論の解析は,それがJohnson-Mehl-Avrami-Kolmogorovモデルと活性化エネルギーによって説明できることを示し,再結晶の活性化エネルギーを,63.4kJ/mol程度と計算した。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *マグネシウム合金 ,  *冷間鍛造 ,  *焼なまし ,  *成形性 ,  *機械的性質 ,  結晶粒度 ,  再結晶 ,  活性化エネルギー ,  集合組織 ,  結晶粒微細化 ,  *引張成形 ,  恒温熱処理
準シソーラス用語： 静的再結晶

分類 (3件)： 鍛造技術  (WC05020H) ,  熱処理技術  (WC03020T) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (7件)： 冷間鍛造 ,  焼鈍 ,  マグネシウム合金 ,  強化 ,  ストレッチ ,  成形性 ,  機械的性質