水溶性の単分散酸化ランタニドのサブミクロ球: PVP補助水熱合成,サイズ制御および発光特性

Water-Soluble Monodispersed Lanthanide Oxide Submicrospheres: PVP-Assisted Hydrothermal Synthesis, Size-Control and Luminescence Properties

著者 (9件)： CUI Ying (Inst. of Process Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  CUI Ying (Graduate Univ., Chinese Acad. of Sci.) ,  LAI Xiaoyong (Inst. of Process Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  LI Li (Inst. of Process Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  HU Zhudong (Inst. of Process Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  WANG Shuo (Inst. of Process Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  HALPERT Jonathan E. (Inst. of Process Engineering, Chinese Acad. of Sci., Beijing, CHN) ,  YU Ranbo (Univ. Sci. and Technol. Beijing, Beijing, Chin) ,  WANG Dan (Inst. of Process Engineering, Chinese Acad. of Sci., Beijing, CHN)
資料名： ChemPhysChem  (ChemPhysChem)
巻： 13  号： 10  ページ： 2610-2614  発行年： 2012年07月16日 
JST資料番号： W1265A  ISSN： 1439-4235  CODEN： CPCHFT  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 沈殿剤として尿素,表面活性剤としてポリ(N-ビニル-2-ピロリドン)(PVP)を用いる水熱法によって,140~430nmサイズの単分散酸化ランタニドのサブミクロン粒子を合成した。この単分散コロイド球の生成機構を走査型と透過型電子顕微鏡(SEMとTEM)およびX線回折(XRD)によって研究した結果,LaMerモデルとPVPが均一でせまいサイズ分布の粒子生成に重要な役割を果たしていることがわかった。その上,水溶性のEu³⁺をドープしたY₂O₃サブミクロン粒子は完全な球状になり,サイズ分布もせまく均一な大きさになった。この方法によって合成したY₂O₃サブミクロン球は610nmに強い発光を示すので,蛍光発光体,電界発光ディスプレイあるいは薬物標識やプローブとして有効である。

シソーラス用語： *酸化イットリウム ,  硝酸 ,  *溶解 ,  *ポリビニルピロリドン ,  沈殿 ,  ドーピング ,  ユウロピウム ,  *ナノ粒子 ,  水熱合成 ,  粒径 ,  *粒度分布 ,  分散【dispersion】 ,  電子顕微鏡観察 ,  X線回折 ,  水溶性 ,  *光ルミネセンス ,  蛍光体 ,  ELディスプレイ ,  薬物 ,  蛍光標識 ,  脂肪族アルコール ,  ウレア化合物
準シソーラス用語： *ナノスフェア ,  単分散

分類 (5件)： 固-液界面  (CB12050B) ,  酸化物の結晶成長  (BK13050I) ,  原子・分子のクラスタ  (BH09030O) ,  無機化合物のルミネセンス  (BM08093J) ,  入出力装置  (JC04050U)

物質索引 (2件)： エタノール ,  尿素

タイトルに関連する用語 (10件)： 水溶性 ,  単分散 ,  酸化 ,  ランタニド ,  サブ ,  ミクロ球 ,  PVP ,  水熱合成 ,  サイズ制御 ,  発光特性