高性能レドックススーパーキャパシタ用ポリアニリン/カルボキシメチルセルロースナトリウムナノロッドのその場合成

In situ synthesis of polyaniline/sodium carboxymethyl cellulose nanorods for high-performance redox supercapacitors

著者 (6件)： PENG Hui (Key Lab. of Eco-Environment-Related Polymer Materials of Ministry of Education, Key Lab. of Polymer Materials of ...) ,  MA Guofu (Key Lab. of Eco-Environment-Related Polymer Materials of Ministry of Education, Key Lab. of Polymer Materials of ...) ,  YING Wenmei (Key Lab. of Eco-Environment-Related Polymer Materials of Ministry of Education, Key Lab. of Polymer Materials of ...) ,  WANG Aidi (Key Lab. of Eco-Environment-Related Polymer Materials of Ministry of Education, Key Lab. of Polymer Materials of ...) ,  HUANG Haohao (Key Lab. of Eco-Environment-Related Polymer Materials of Ministry of Education, Key Lab. of Polymer Materials of ...) ,  LEI Ziqiang (Key Lab. of Eco-Environment-Related Polymer Materials of Ministry of Education, Key Lab. of Polymer Materials of ...)
資料名： Journal of Power Sources  (Journal of Power Sources)
巻： 211  ページ： 40-45  発行年： 2012年08月01日 
JST資料番号： B0703B  ISSN： 0378-7753  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ポリアニリン/カルボキシメチルセルロースナトリウム(PANI/CMC)ナノロッドを,重合鋳型としてカルボキシメチルセルロースナトリウムの存在下にて,アニリンのその場酸化重合により合成した。ナノロッドの構造およびモルホロジーは,TEM,FE-SEMおよびXRDによりキャラクタリゼーションした。この複合材料ナノロッドの大きさおよび形状は,直径100nmにて均一であった。またその電気化学特性についても,サイクリックボルタンメトリおよび定電流充/放電測定により調べた。CMC20wt%にて調製したPANI/CMCナノロッドの比キャパシタンスは,451.25Fg^-1ほどの高さであった。そのキャパシタンスは,電流密度1Ag^-1にて1000サイクル後も,300Fg^-1以上の高さを保持した。これら新規ナノロッドは,スーパーキャパシタデバイス用途用に有望である。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *電力コンデンサ ,  *ポリアニリン ,  カルボキシメチルセルロース ,  ナトリウム化合物 ,  ナノロッド ,  酸化重合 ,  充放電サイクル ,  静電容量 ,  その場重合
準シソーラス用語： *スーパーキャパシタ ,  カルボキシメチルセルロースナトリウム