Onset coarsening-coalescence kinetics of ZrO₂ and less refractory TiO₂ nanoparticles: Effect of homologous temperature and phase transformation

著者 (5件)： CHEN Tzu-jung (Dep. of Materials and Optoelectronic Sci., National Sun Yat-sen Univ., Kaohsiung 80424, Taiwan, TWN) ,  LU Jer-han (Dep. of Materials and Optoelectronic Sci., National Sun Yat-sen Univ., Kaohsiung 80424, Taiwan, TWN) ,  LU Hui-di (Dep. of Materials and Optoelectronic Sci., National Sun Yat-sen Univ., Kaohsiung 80424, Taiwan, TWN) ,  LIU I-lung (Dep. of Materials and Optoelectronic Sci., National Sun Yat-sen Univ., Kaohsiung 80424, Taiwan, TWN) ,  SHEN Pouyan (Dep. of Materials and Optoelectronic Sci., National Sun Yat-sen Univ., Kaohsiung 80424, Taiwan, TWN)
資料名： Journal of the European Ceramic Society  (Journal of the European Ceramic Society)
巻： 32  号： 4  ページ： 795-805  発行年： 2012年04月 
JST資料番号： E0801B  ISSN： 0955-2219  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ZrO₂(主として正方晶-(t)対称,30~50nm)と耐火性がより低いTiO₂アナターゼナノ粒子(20~50nm)の大気中700~1000°Cでの等温焼成による比表面積変化をN₂吸着-脱着ヒステリシス等温線により求めた。ナノ粒子はTiO₂の場合顕著な相変態無しに数分以内に粗大化-合体を示したが,ZrO₂の場合単斜晶(m-)対称への顕著な変態を示した。この様なプロセスのZrO₂の見掛けの活性化エネルギー(77±23kJ/mol)はTiO₂ナノ粒子(56±3kJ/mol)よりもそれほど大きくなく,変態塑性に起因した。本研究のZrO₂とTiO₂ナノ粒子の粗大化/合体のための最低温度は各々710°Cと641°Cと評価された。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.