文献

J-GLOBAL ID：201202226162645221   整理番号：12A1391128

階層組織化γ-AlOOH中空球体のイオン液体支援水熱作製

Ionic liquid assisted hydrothermal fabrication of hierarchically organized γ-AlOOH hollow sphere

著者 (5件)： TANG Zhe (State Key Lab. of Heavy Oil Processing, Key Lab. of Catalysis, China National Petroleum Corp. (CNPC), China Univ. of ...) ,  LIU Yunqi (State Key Lab. of Heavy Oil Processing, Key Lab. of Catalysis, China National Petroleum Corp. (CNPC), China Univ. of ...) ,  LI Guangci (State Key Lab. of Heavy Oil Processing, Key Lab. of Catalysis, China National Petroleum Corp. (CNPC), China Univ. of ...) ,  HU Xiaofu (State Key Lab. of Heavy Oil Processing, Key Lab. of Catalysis, China National Petroleum Corp. (CNPC), China Univ. of ...) ,  LIU Chenguang (State Key Lab. of Heavy Oil Processing, Key Lab. of Catalysis, China National Petroleum Corp. (CNPC), China Univ. of ...)
資料名： Materials Research Bulletin  (Materials Research Bulletin)
巻： 47  号： 11  ページ： 3177-3184  発行年： 2012年11月 
JST資料番号： B0954A  ISSN： 0025-5408  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： くえん酸一水和物(CAM)中のイオン液体支援水熱合成法によってナノフレーク状多孔質表面組織を有する階層組織化γ-AlOOH中空球体を合成することができた。イオン液体[bmim]⁺Cl^-が反応粒子とのその強い相互作用により生成物の形態に重要な役割を演じることが見いだされた。試料をX線回折(XRD),Fourier変換赤外分光法(FT-IR),走査電子顕微鏡(SEM)および透過型電子顕微鏡法(TEM)によってキャラクタリゼーションした。結果によると生成物は狭い粒子サイズ分布(500~900nmの粒子直径),高い比表面積(240.5m²/g)および大きな細孔体積(0.61cm³/g)を有していた。生成物を550°Cで3時間焼成することによって対応するγ-Al₂O₃中空球体を得ることができた。反応温度,反応持続時間,CAMおよび尿素などγ-AlOOH中空球体材料の提案形成機構および他の影響要因を検討した。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： 階層構造 ,  *酸化物 ,  *水酸化物 ,  *アルミニウム化合物 ,  *球 ,  *中空体 ,  イオン液体 ,  水熱合成
準シソーラス用語： オキシ水酸化物 ,  *中空球

分類 (2件)： コロイド化学一般  (CB11010C) ,  塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (7件)： 階層 ,  組織化 ,  中空球 ,  イオン液体 ,  支援 ,  水 ,  作製