ゾル-ゲル法由来のチタニア木材-無機複合材料の難燃性

Fire retardancy of sol-gel derived titania wood-inorganic composites

著者 (7件)： SHABIR MAHR Muhammad (BAM Federal Inst. for Materials Res. and Testing, Unter den Eichen 44-46, 12203, Berlin, DEU) ,  SHABIR MAHR Muhammad (Georg-August-University Goettingen, Wood Biology and Wood Products, Burckhardt Inst., Buesgenweg 4, 37077 ...) ,  HUEBERT Thomas (BAM Federal Inst. for Materials Res. and Testing, Unter den Eichen 44-46, 12203, Berlin, DEU) ,  SABEL Martin (BAM Federal Inst. for Materials Res. and Testing, Unter den Eichen 44-46, 12203, Berlin, DEU) ,  SCHARTEL Bernhard (BAM Federal Inst. for Materials Res. and Testing, Unter den Eichen 44-46, 12203, Berlin, DEU) ,  BAHR Horst (BAM Federal Inst. for Materials Res. and Testing, Unter den Eichen 44-46, 12203, Berlin, DEU) ,  MILITZ Holger (Georg-August-University Goettingen, Wood Biology and Wood Products, Burckhardt Inst., Buesgenweg 4, 37077 ...)
資料名： Journal of Materials Science  (Journal of Materials Science)
巻： 47  号： 19  ページ： 6849-6861  発行年： 2012年10月 
JST資料番号： B0722A  ISSN： 0022-2461  CODEN： JMTSAS  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： ゾル-ゲル技術は,改良された熱的,燃焼特性を持つ新規木材製の無機複合材料を製造するために使用した。複合材料はチタン(IV)イソプロポキシドから誘導したナノスケール前駆体溶液をマツ辺材木材に含浸させ,引き続き熱硬化処理して製造した。熱的,燃焼特性は,熱解析とコーン熱量計により評価した。一方,燃焼性は酸素指数(LOI)およびUL94試験により特性化した。ピーク熱放出率が緩やかに減少し,チタニア系堆積物の適切な保護層の作用により火炎伝播の観点から難燃性の可能性を示した。これらの複合材料のLOI(酸素指数)値は未処理の木材の23容量%と比較して最大38容量%まで増加した。難燃性の性能は火災シナリオに依存し,木材の負荷および,複合材料内のチタニア層の無亀裂堆積により顕著に左右される。Copyright 2012 Springer Science+Business Media, LLC Translated from English into Japanese by JST.

シソーラス用語： *マツ属 ,  辺材 ,  *木材 ,  チタン化合物 ,  アルコラート ,  脂肪族アルコール ,  硝酸 ,  前駆体 ,  *ゾル-ゲル法 ,  *含浸 ,  熱硬化 ,  燃焼性 ,  酸素指数 ,  UL規格 ,  *酸化チタン ,  *複合材料 ,  *難燃性
準シソーラス用語： LOI【酸素】 ,  チタニア ,  松

分類 (1件)： 木質材料の製造・加工一般  (FF05031B)

物質索引 (2件)： イソプロパノール ,  テトライソプロポキシチタン

タイトルに関連する用語 (5件)： ゾル-ゲル法 ,  チタニア ,  木材 ,  複合材料 ,  難燃性