Synthesis, characterization and magnetic performance of Co-incorporated ordered mesoporous carbons

著者 (5件)： LIU Zhi (Inst. of Chemistry for Functionalized Materials, Fac. of Chemistry and Chemical Engineering, Liaoning Normal Univ. ...) ,  SONG Yan (Inst. of Chemistry for Functionalized Materials, Fac. of Chemistry and Chemical Engineering, Liaoning Normal Univ. ...) ,  YANG Yuan (Inst. of Chemistry for Functionalized Materials, Fac. of Chemistry and Chemical Engineering, Liaoning Normal Univ. ...) ,  MI Junhua (Inst. of Chemistry for Functionalized Materials, Fac. of Chemistry and Chemical Engineering, Liaoning Normal Univ. ...) ,  DENG Liping (Inst. of Chemistry for Functionalized Materials, Fac. of Chemistry and Chemical Engineering, Liaoning Normal Univ. ...)
資料名： Materials Research Bulletin  (Materials Research Bulletin)
巻： 47  号： 2  ページ： 274-278  発行年： 2012年02月 
JST資料番号： B0954A  ISSN： 0025-5408  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ワンポット自己組織化戦略により,磁性枠組みを含むCo組込み秩序化メソ多孔性炭素(Co-OMC)を合成した。窒素吸着,X線回折(XRD),透過型電子顕微鏡(TEM),熱重量分析(TG),磁力計測定により,結果としてのメソ構造コバルト/炭素複合材料の炭素マトリックス,吸着特性,磁性に及ぼすコバルト含量影響を調べた。結果では,高コバルト含量(18.0wt%のような)のメソ多孔性複合材料は秩序化均一多孔性構造(5.3nm),高表面積(最大687m²/g),高孔体積(最大0.54cm³/g)を持つことを示した。サイズ4~9nmのコバルトナノ粒子はメソ多孔性炭素のメソ孔や壁内に制限される。これらの材料は典型的な強磁性とを示した。飽和磁化強度は,コバルト含量変更により容易に調整できる。炭化温度はCo-OMCの構造特性や磁性に顕著な影響を持つ。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： ワンポット合成 ,  自己組織化 ,  *複合材料 ,  *コバルト化合物 ,  *硝酸塩 ,  *材料 ,  *多孔質体 ,  *炭素材 ,  *強磁性 ,  *規則化 ,  窒素 ,  吸着 ,  X線回折 ,  透過型電子顕微鏡 ,  熱重量分析 ,  磁力計 ,  マトリックス【母体】 ,  含有量 ,  表面積 ,  体積 ,  飽和磁化 ,  反応温度
準シソーラス用語： *硝酸コバルト ,  *メソ多孔質体 ,  *秩序化 ,  細孔容積 ,  炭化温度

分類 (3件)： 炭素とその化合物  (YB02060D) ,  塩  (CD01050V) ,  その他の無機化合物の磁性  (BM06060P)

タイトルに関連する用語 (5件)： CO ,  組込み ,  秩序化メソ多孔性炭素 ,  特性化 ,  磁気性能