Al-3.5Cu-0.4Mg(重量%)合金のGe添加の効果

The effect of Ge addition on Al-3.5Cu-0.4Mg (wt.%) alloy

著者 (6件)： LIAO Zhongquan (School of Materials Sci. and Engineering, Central South Univ., Changsha, Hunan 410083, People’s Republic of China) ,  LI Shichen (School of Materials Sci. and Engineering, Central South Univ., Changsha, Hunan 410083, People’s Republic of China) ,  ZHENG Ziqiao (School of Materials Sci. and Engineering, Central South Univ., Changsha, Hunan 410083, People’s Republic of China) ,  CAI Biao (School of Materials Sci. and Engineering, Central South Univ., Changsha, Hunan 410083, People’s Republic of China) ,  ZHONG Shen (School of Materials Sci. and Engineering, Central South Univ., Changsha, Hunan 410083, People’s Republic of China) ,  LUO Xianfu (School of Materials Sci. and Engineering, Central South Univ., Changsha, Hunan 410083, People’s Republic of China)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 66  号： 7  ページ： 447-450  発行年： 2012年04月 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Al-3.5Cu-0.4MgにGeを微量(0.2重量%)添加すると,その強度と伸びが著しく増加した。時効処理したAl-3.5Cu-0.4Mg-0.2Ge(重量%)合金を150°Cに加熱すると優れた引張強さを示した。透過電子顕微鏡観察の結果,これらの性質は,ナノスケールの析出物の高密度ミクロ組織と,これら析出物の優れた粗大化阻止と関係していること,すなわち時効処理したAl-3.5Cu-0.4Mg-0.2Ge(重量%)合金の中のGeがナノスケールの析出物の形成を促し,S′析出物の形成を抑えたからであることがわかった。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *アルミニウム合金 ,  銅含有合金 ,  マグネシウム含有合金 ,  ゲルマニウム添加合金 ,  *引張強さ ,  *伸び率 ,  *時効処理 ,  ナノ構造 ,  析出物 ,  密度 ,  金属組織 ,  結晶粒粗大化 ,  押込硬さ ,  時間依存性 ,  距離 ,  析出 ,  *中間相
準シソーラス用語： *Sプライム相 ,  Vickers硬度 ,  *ナノ析出