鋳造Ni基超合金のミクロ組織と特性の長期間の熱曝露応答

Long-term thermal exposure responses of the microstructure and properties of a cast Ni-base superalloy

著者 (6件)： QIN X.z. (Inst. of Metal Res., Chinese Acad. of Sciences, 72 Wenhua Road, Shenyang 110016, CHN) ,  GUO J.t. (Inst. of Metal Res., Chinese Acad. of Sciences, 72 Wenhua Road, Shenyang 110016, CHN) ,  YUAN C. (Inst. of Metal Res., Chinese Acad. of Sciences, 72 Wenhua Road, Shenyang 110016, CHN) ,  HOU J.s. (Inst. of Metal Res., Chinese Acad. of Sciences, 72 Wenhua Road, Shenyang 110016, CHN) ,  ZHOU L.z. (Inst. of Metal Res., Chinese Acad. of Sciences, 72 Wenhua Road, Shenyang 110016, CHN) ,  YE H.q. (Inst. of Metal Res., Chinese Acad. of Sciences, 72 Wenhua Road, Shenyang 110016, CHN)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 543  ページ： 121-128  発行年： 2012年05月01日 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： K446合金の長期間の熱曝露中のミクロ組織の変化およびミクロ組織-性質の関係を調べる。γ′析出の粗大化速度は曝露温度の上昇とともに増加するが,曝露時間の増加とともに減少する。一次MC炭化物は優れた安定性を示し,性質に極僅かな影響を及ぼす2つの反応形式で極僅かな程度分解する。TCP-μ相が針と粒の形状に過飽和マトリックスから析出し,曝露の延長にともない著しい変化を起こす。つまり,粒界(GBs)の近くのμ相は元素の不均一な分布のため粒内のそれよりゆっくりと変化する。加えて,μ相の析出を測定したが,本合金のγ′粗大化より機械的性質により有害である。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *ニッケル合金 ,  *超合金 ,  *金属組織 ,  曝露 ,  γプライム相 ,  温度依存性 ,  時間依存性 ,  析出物 ,  炭化物 ,  中間相 ,  μ相 ,  クロム含有合金 ,  アルミニウム含有合金 ,  チタン含有合金 ,  ニオブ含有合金 ,  モリブデン含有合金 ,  タングステン含有合金 ,  降伏強さ ,  伸び率 ,  クリープ強さ ,  結晶粒粗大化 ,  *粒界析出
準シソーラス用語： TCP相 ,  ニッケル基超合金 ,  *高温曝露 ,  *高温暴露 ,  鋳造合金

分類 (2件)： 組織的硬化現象  (WB01020C) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： 鋳造 ,  Ni基超合金 ,  ミクロ組織 ,  熱曝露 ,  応答