NiTi基板上の熱硬化させナノクレイで強化した高分子電解質膜の成形性

Formability of thermally cured and of nanoclay-reinforced polyelectrolyte films on NiTi substrates

著者 (6件)： LACKMANN J. (Univ. of Paderborn, Lehrstuhl fuer Werkstoffkunde (Materials Science), Pohlweg 47-49, 33098, Paderborn, DEU) ,  NIENDORF T. (Univ. of Paderborn, Lehrstuhl fuer Werkstoffkunde (Materials Science), Pohlweg 47-49, 33098, Paderborn, DEU) ,  MAXISCH M. (Univ. of Paderborn, Technical and Macromolecular Chemistry, Dep. of Chemistry, Warburger Strasse 100, D-33098 ...) ,  REGENSPURGER R. (Univ. of Paderborn, Technical and Macromolecular Chemistry, Dep. of Chemistry, Warburger Strasse 100, D-33098 ...) ,  GRUNDMEIER G. (Univ. of Paderborn, Technical and Macromolecular Chemistry, Dep. of Chemistry, Warburger Strasse 100, D-33098 ...) ,  MAIER H. J. (Univ. of Paderborn, Lehrstuhl fuer Werkstoffkunde (Materials Science), Pohlweg 47-49, 33098, Paderborn, DEU)
資料名： Journal of Materials Science  (Journal of Materials Science)
巻： 47  号： 1  ページ： 151-161  発行年： 2012年01月 
JST資料番号： B0722A  ISSN： 0022-2461  CODEN： JMTSAS  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究は硬化とナノサイズの板状粘土粒子で強化して改質した高分子電解質薄膜の成形性を評価した。生物医学応用のために改質した高分子電解質コーティングの適合性を調べるため,膜を多結晶と単結晶NiTi50.9at%基板に適用し,擬似体液(Hank溶液)中で繰り返し引張荷重下で機械的に変形させた。その場電子後方散乱回折,その場共焦点レーザー走査顕微鏡,光弾性変調赤外反射吸収分光及びエリプソメトリ測定により欠陥生成を調べた。機械的試験前後の基板と膜の観察結果から,引張サイクル試験過程での欠陥生成は基板と膜の性質に関連した。欠陥は顕著な立体的変化の範囲内で多結晶と単結晶基板の上の未改質で硬化した高分子電解質膜に特に発生した。対照的に,ナノクレイ改質したコーティングには欠陥が無く,成形性の著しい向上を示し,それは高分子電解質マトリックス内の強化粘土板状粒子と関連した。Copyright 2011 Springer Science+Business Media, LLC Translated from English into Japanese by JST.

シソーラス用語： *ニッケル合金 ,  チタン含有合金 ,  *形状記憶合金 ,  基板 ,  高分子膜 ,  ナノ粒子 ,  粘土 ,  *補強材料 ,  *成形性 ,  利用 ,  *医用素材 ,  生体適合性 ,  腐食試験 ,  欠陥検査
準シソーラス用語： Hanks溶液 ,  *ナノクレイ ,  強化材 ,  *高分子電解質膜 ,  生物医学応用