Bending behavior of TiZrNiCuBe bulk metallic glass

著者 (8件)： HUANG Yongjiang (State Key Lab. of Advanced Welding and Joining, Harbin Inst. of Technol., Harbin 150001, CHN) ,  HUANG Yongjiang (Key Lab. of Micro-Systems and Micro-Structures Manufacturing, Harbin Inst. of Technol., Ministry of Education, CHN) ,  WANG Dongjun (State Key Lab. of Advanced Welding and Joining, Harbin Inst. of Technol., Harbin 150001, CHN) ,  WANG Dongjun (Key Lab. of Micro-Systems and Micro-Structures Manufacturing, Harbin Inst. of Technol., Ministry of Education, CHN) ,  WANG Dapeng (Automotive Res. Inst. of China FAW Group Corp., Changchun 130011, CHN) ,  ZHANG Zhixiong (State Key Lab. of Advanced Welding and Joining, Harbin Inst. of Technol., Harbin 150001, CHN) ,  SHEN Jun (State Key Lab. of Advanced Welding and Joining, Harbin Inst. of Technol., Harbin 150001, CHN) ,  SHEN Jun (Key Lab. of Micro-Systems and Micro-Structures Manufacturing, Harbin Inst. of Technol., Ministry of Education, CHN)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 541  ページ： 359-364  発行年： 2012年11月15日 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 曲げ試験中のTiベースのバルク金属ガラス(BMG)の変形挙動を調査した。曲げ温度は,本研究におけるBMGの変形挙動に重要な役割を果たす。曲げ温度の上昇に伴い,BMGは脆性-延性-脆性転移を示した。(過冷却液体領域である)350および360°Cの曲げ温度の場合,BMG試料は均一に変形し,優れた変形能力を示した。さらに,曲げ試験後,高温によるナノ結晶化および変形応力の観察も行った。温度の上昇に伴い,変形後の試料の破壊形態は,静脈状のパターンから川状あるいは亀裂状のパターンへ変化した。本BMG材料の曲げ変形挙動を,試験中の構造変化を基に議論した。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *非晶質合金 ,  *チタン合金 ,  ジルコニウム含有合金 ,  ニッケル含有合金 ,  銅含有合金 ,  ベリリウム含有合金 ,  *曲げ変形 ,  延性-脆性遷移 ,  結晶化 ,  ナノ結晶 ,  応力 ,  *変形組織 ,  変化 ,  形態 ,  破壊 ,  過冷却液体 ,  *バルク金属ガラス
準シソーラス用語： *バルク非晶質合金 ,  構造変化 ,  破壊形態