304オーステナイト系ステンレス鋼における双晶化およびマルテンサイト

Twinning and martensite in a 304 austenitic stainless steel

著者 (6件)： SHEN Y.f. (Key Lab. for Anisotropy and Texture of Materials (MOE), Northeastern Univ., Shenyang 110004, CHN) ,  SHEN Y.f. (Computational Sci. and Mathematics Div., Pacific Northwest National Lab., Richland, WA 99352, USA) ,  LI X.x. (Key Lab. for Anisotropy and Texture of Materials (MOE), Northeastern Univ., Shenyang 110004, CHN) ,  SUN X. (Computational Sci. and Mathematics Div., Pacific Northwest National Lab., Richland, WA 99352, USA) ,  WANG Y.d. (Key Lab. for Anisotropy and Texture of Materials (MOE), Northeastern Univ., Shenyang 110004, CHN) ,  ZUO L. (Key Lab. for Anisotropy and Texture of Materials (MOE), Northeastern Univ., Shenyang 110004, CHN)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 552  ページ： 514-522  発行年： 2012年08月30日 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 304Lステンレス鋼の二つの異なるひずみ速度での引張変形中の金属組織特性および変形挙動を,中断引張試験,電子後方散乱回折(EBSD)及び透過型電子顕微鏡(TEM)観察を用いて研究した。変形過程の種々の段階での変態マルテンサイトと変形双晶の体積率を,X線回折法とTEM観察を用いて測定した。マルテンサイトの体積率は,ひずみの増加により単調に増加するが,ひずみ速度の増加に伴って減少することが分かった。一方,双晶体積率は,57%未満のひずみレベルではひずみの増加と共に増加する。それを超えると,双晶体積率は,ひずみの増加に伴って減少する。慎重なTEM観察により,積層欠陥(SF)と双晶がマルテンサイトの核生成の前に優先的に発生することがわかった。一方,ε-マルテンサイトとα′-マルテンサイトの両方が,変形組織で観察されたが,それは,応力誘起変態とひずみ誘起変態の共存を意味する。また,加工硬化に及ぼす双晶とマルテンサイト変態の影響ならびに積層欠陥,双晶およびマルテンサイト変態間の関係を議論した。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *オーステナイト系ステンレス鋼 ,  引張変形 ,  *マルテンサイト変態 ,  *変形双晶 ,  体積率 ,  積層欠陥 ,  加工硬化 ,  変形組織 ,  応力歪曲線 ,  *引張試験 ,  歪速度
準シソーラス用語： *AISI304L ,  応力誘起変態 ,  歪依存性 ,  歪速度依存性 ,  歪誘起変態

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (3件)： オーステナイト系ステンレス鋼 ,  双晶化 ,  マルテンサイト