放電加工により作製した高分散Ni-Mn-Ga粉末の構造と磁気特性

Structure and magnetic properties of highly dispersed Ni-Mn-Ga powders prepared by spark-erosion

著者 (7件)： PEREKOS A. E. (Inst. of Metal Physics NAS of Ukraine, 36 Vernadskogo Blvd., 03142 Kiev, UKR) ,  CHERNENKO V. A. (Departamento de Electricidad y Electronica, Universidad del Pais Vasco UPV/EHU, Apartado 644, E-48080 Bilbao, ESP) ,  BUNYAEV S. A. (IFIMUP-IN, Departamento do Fisica, Universidade do Porto, Rua do Campo Alegre 687, 4169-007 Porto, PRT) ,  ZALUTSKIY V. P. (Inst. of Metal Physics NAS of Ukraine, 36 Vernadskogo Blvd., 03142 Kiev, UKR) ,  RUZHITSKAYA T. V. (Inst. of Metal Physics NAS of Ukraine, 36 Vernadskogo Blvd., 03142 Kiev, UKR) ,  BOITSOV O. F. (Inst. of Metal Physics NAS of Ukraine, 36 Vernadskogo Blvd., 03142 Kiev, UKR) ,  KAKAZEI G. N. (IFIMUP-IN, Departamento do Fisica, Universidade do Porto, Rua do Campo Alegre 687, 4169-007 Porto, PRT)
資料名： Journal of Applied Physics  (Journal of Applied Physics)
巻： 112  号： 9  ページ： 093909-093909-7  発行年： 2012年11月01日 
JST資料番号： C0266A  ISSN： 0021-8979  CODEN： JAPIAU  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： Ni_50.3Mn₃₀Ga_19.7の高分散粉末を放電加工によりエタノール,水,およびケロセン中で作製した。粉末粒子はほとんどが球形状で最大約1μmをもつ広いサイズ分布を有した。作製したままの状態では,X線回折により2系列のピークを観測した。それらはバルクNi-Mn-Gaに存在する二つの規則相の乱れに関係した:高温L2₁オーステナイト相と低温L1₀マルテンサイト相。アニールはピークの半値幅を小さくし,L1₀/L2₁強度比を増した。作製したままの粉末は磁気的に明確な超常磁性挙動を示し,アニール後,強磁性に変化した。これらの性質は,同一組成について機械的に分散させた粉末や急冷リボンのものとは全く異なっていた。放電加工条件,特に10⁹K/sに達する冷却速度は,混合相状態,はるかに高い原子不規則性を形成し,いろいろな種類の構造不均一性を出現させた。(翻訳著者抄録)

シソーラス用語： *ニッケル合金 ,  マンガン含有合金 ,  ガリウム含有合金 ,  *金属粉末 ,  *結晶構造 ,  *磁気的性質 ,  *放電加工 ,  粒子 ,  形態 ,  粒度分布 ,  X線回折 ,  規則相 ,  オーステナイト ,  マルテンサイト ,  焼なまし ,  超常磁性 ,  強磁性 ,  急冷 ,  リボン ,  冷却速度 ,  *分散系 ,  磁化 ,  温度依存性 ,  曲線 ,  結晶粒 ,  結晶粒径
準シソーラス用語： オーステナイト相 ,  マルテンサイト相 ,  形状 ,  磁化曲線 ,  *磁気特性 ,  磁場依存性

分類 (2件)： 金属の結晶構造  (BK06000V) ,  磁気的性質  (WB02020J)

タイトルに関連する用語 (5件)： 放電加工 ,  作製 ,  Ni-Mn-Ga ,  粉末 ,  磁気特性