異なるMn含有量の摩擦撹拌処理したストリップキャスト5083アルミニウム合金の熱間変形挙動

Hot deformation behavior of friction-stir processed strip-cast 5083 aluminum alloys with different Mn contents

著者 (4件)： GARCIA-BERNAL M.a. (Dep. of Aeronautical Engineering, Instituto Politecnico Nacional, ESIME Unidad Ticoman, Av. Ticoman No. 600, Col. ...) ,  MISHRA R.s. (Dep. of Materials Sci. and Engineering, Missouri Univ. of Sci. and Technol., 1870 Miner Circle, Rolla, MO 65409-0340 ...) ,  VERMA R. (Manufacturing Systems Res. Lab, General Motors R&D, 30500 Mound Road, Warren, MI 48090, USA) ,  HERNANDEZ-SILVA D. (Dep. of Metallurgical Engineering, Instituto Politecnico Nacional, ESIQIE, Apdo. Postal 118-392, 07738 Mexico D.F., MEX)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 534  ページ： 186-192  発行年： 2012年02月01日 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 微細結晶粒5083アルミニウム合金は,自動車や航空宇宙産業で軽量金属板部品の超塑性成形(SPF)材として利用される最も一般的なAl-Mg系合金である。微細結晶粒板は,従来から圧延板材を大規模な冷間圧延処理により高コストで工業的に製造されてきた。摩擦撹拌プロセスは,板連続鋳造(CC)法などで製造した鋳造合金の組織微細化を実現する非常に効率的なサーモメカニカルプロセスである。本研究は,3種類のMn含有量の異なるCC-5083アルミニウム合金の超塑性特性に及ぼす摩擦撹拌プロセスの効果を検討した。摩擦撹拌処理により,約3μm未満の粒径を持つ非常に微細な組織が得られた。引張試験を10^-1s^-1の歪み速度で行ったところ,3種類の合金全てが600%以上の伸びを示した。800パーセントの最大引張伸びが,最低Mn含有量合金で490°C,歪み速度3×10^-2s^-1条件で実現した。500°C以上の高温では,微細組織の安定性が重要な関心事である。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： 表面加工 ,  *アルミニウム合金 ,  *鋳物 ,  金属板 ,  *高温変形 ,  マンガン添加合金 ,  成形 ,  塑性加工 ,  マグネシウム含有合金 ,  加工熱処理 ,  結晶粒微細化 ,  伸び率 ,  超塑性 ,  歪速度 ,  連鋳鋳片 ,  鋳造 ,  ストリップキャスティング ,  帯板 ,  摩擦撹拌処理
準シソーラス用語： *AA5083 ,  超塑性成形

分類 (2件)： 機械的性質  (WB02030U) ,  鋳造に関する各種技術  (WC01040B)

タイトルに関連する用語 (7件)： Mn ,  含有量 ,  摩擦撹拌処理 ,  ストリップ ,  キャスト ,  アルミニウム合金 ,  変形挙動