Responsive plasma polymerized ultrathin nanocomposite films

著者 (6件)： ANDERSON Kyle D. (School of Materials Sci. and Engineering, Georgia Inst. of Technol., Atlanta, GA 30332, USA) ,  WEBER Robert B. (School of Materials Sci. and Engineering, Georgia Inst. of Technol., Atlanta, GA 30332, USA) ,  MCCONNEY Michael E. (Materials and Manufacturing Directorate, Air Force Res. Lab., Wright-Patterson Air Force Base, Dayton, OH 45433-7702 ...) ,  JIANG Hao (Materials and Manufacturing Directorate, Air Force Res. Lab., Wright-Patterson Air Force Base, Dayton, OH 45433-7702 ...) ,  BUNNING Timothy J. (Materials and Manufacturing Directorate, Air Force Res. Lab., Wright-Patterson Air Force Base, Dayton, OH 45433-7702 ...) ,  TSUKRUK Vladimir V. (School of Materials Sci. and Engineering, Georgia Inst. of Technol., Atlanta, GA 30332, USA)
資料名： Polymer  (Polymer)
巻： 53  号： 21  ページ： 4686-4693  発行年： 2012年09月28日 
JST資料番号： D0472B  ISSN： 0032-3861  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： プラズマ強化化学気相成長法を用いて,N-イソプロピルアクリルアミド(NIPAAM)およびチタンイソプロポキシド単量体の応答性光学特性をもつ応答性超薄膜へのプラズマ重合を報告した。複合超薄膜は,1.60から1.95へ屈折率を変化させる大きな窓を有していた。著者らは,これらの高分子膜が,周期的な環境湿度の変化の関数として,それらの厚さに対して迅速(2s以下の遷移時間)で,大きく,可逆的で,および再現性の変化および屈折率を示すことを実証した。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *プラズマ重合 ,  *複合膜 ,  *ナノ複合材料 ,  *ポリイソプロピルアクリルアミド ,  高分子有機-無機ハイブリッド ,  有機チタン化合物 ,  高分子薄膜 ,  ポリプロピレン ,  *熱応答 ,  化学蒸着 ,  気相成長 ,  *光応答性高分子 ,  屈折率 ,  表面分析 ,  湿度 ,  湿度センサ ,  膜厚

分類 (1件)： 高分子固体の物理的性質  (CG02024U)

物質索引 (2件)： N-イソプロピルアクリルアミド ,  チタンテトライソプロポキシド

タイトルに関連する用語 (3件)： 応答性 ,  プラズマ重合 ,  ナノ複合膜