アルミナを多量に添加したイットリア安定化ジルコニアの高温相安定性と化学分析

High temperature phase stability and chemical analysis of the highly doped yttria stabilized zirconia with alumina

著者 (7件)： NAZARPOUR S. (INRS energie, materiaux et telecommunications, 1650 boulevard Lionel Boulet, Varennes, QC, J3X 1S2 Canada) ,  LOPEZ-GANDARA C. (Dep. of Electronics, Univ. of Barcelona, Marti i Franques 1, Barcelona 08028, ESP) ,  LOPEZ-GANDARA C. (FAE, Rafael Barradas 19, L’Hospitalet de Llobregat 08908, ESP) ,  RAMOS F.m. (FAE, Rafael Barradas 19, L’Hospitalet de Llobregat 08908, ESP) ,  ZAMANI C. (Dep. of Electronics, Univ. of Barcelona, Marti i Franques 1, Barcelona 08028, ESP) ,  CIRERA A. (Dep. of Electronics, Univ. of Barcelona, Marti i Franques 1, Barcelona 08028, ESP) ,  CHAKER M. (INRS energie, materiaux et telecommunications, 1650 boulevard Lionel Boulet, Varennes, QC, J3X 1S2 Canada)
資料名： Ceramics International  (Ceramics International)
巻： 38  号： 6  ページ： 4813-4818  発行年： 2012年08月 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： YSZの平衡および非平衡相転移を考慮して,YSZの短期間および長期間熱安定性を研究した。YSZの長期間熱安定性を向上するため,電気的処理を導入した。電気的処理では,高温,還元雰囲気下においてYSZに電場を負荷した。処理条件の最適化により,電気抵抗は約40%低減し,熱安定性が劇的に向上した。これらの向上は正方晶準安定相の発生に帰せられた。検討した結果,電気的処理は格子の緩和を誘起することが分かった。この緩和は格子の正方晶性の低下と関連し,準安定相ドメインを有するYSZの正方晶粒を置き換えた。正方晶粒と比べて耐クリープ変形性が高い純安定相および電気抵抗が低い準安定相ドメインにより,これらの向上がもたらされた。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： セラミック ,  酸化イットリウム ,  *酸化ジルコニウム ,  添加物効果 ,  アルミナ ,  依存性 ,  *微細構造 ,  結晶構造 ,  相安定性 ,  相平衡 ,  非平衡状態 ,  熱安定性 ,  電場効果 ,  電気抵抗 ,  準安定相 ,  正方晶系 ,  格子定数 ,  構造緩和 ,  クリープ強さ ,  高温強さ
準シソーラス用語： YSZ【セラミック】 ,  組成依存性 ,  微細組織 ,  非平衡

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： アルミナ ,  イットリア安定化ジルコニア ,  相安定性 ,  化学分析