超臨界水中の18Cr-酸化物分散強化鋼の腐食挙動の研究

Study of the corrosion behavior of a 18Cr-oxide dispersion strengthened steel in supercritical water

著者 (7件)： HU Helong (School of Materials Sci. and Engineering, Univ. of Sci. and Technol. Beijing, Beijing 100083, CHN) ,  ZHOU Zhangjian (School of Materials Sci. and Engineering, Univ. of Sci. and Technol. Beijing, Beijing 100083, CHN) ,  LI Ming (School of Materials Sci. and Engineering, Univ. of Sci. and Technol. Beijing, Beijing 100083, CHN) ,  ZHANG Lefu (School of Nuclear Sci. and Engineering, Shanghai Jiaotong Univ., Shanghai 200240, CHN) ,  WANG Man (School of Materials Sci. and Engineering, Univ. of Sci. and Technol. Beijing, Beijing 100083, CHN) ,  LI Shaofu (School of Materials Sci. and Engineering, Univ. of Sci. and Technol. Beijing, Beijing 100083, CHN) ,  GE Changchun (School of Materials Sci. and Engineering, Univ. of Sci. and Technol. Beijing, Beijing 100083, CHN)
資料名： Corrosion Science  (Corrosion Science)
巻： 65  ページ： 209-213  発行年： 2012年12月 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 超臨界水(600°C/25MPa)中に曝された18Cr-ODS(酸化物分散強化)鋼の腐食挙動を調べた。結果は重量利得は露出時間につれて増大し,放物線則に従うことを示す。外側層,内側層及び拡散層で構成される三重層を試料上に形成する。外側層の相はFe₂O₃とFe₃O₄である。内側層と拡散層はそれぞれ(Fe,Cr)₃O₄とCr₂O₃を含む。亀裂,細孔および剥離を外側層上に観察できた。最後に,酸化機構を議論し決定的要因を与えた。Copyright 2012 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *高合金鋼 ,  *分散強化合金 ,  *クロム含有合金 ,  腐食 ,  *超臨界水 ,  *腐食生成物 ,  多層構造 ,  亀裂 ,  細孔 ,  剥離 ,  酸化
準シソーラス用語： ODS鋼